PEI EFL34HL-BK8065 SABIC INNOVATIVE SINGAPHORE
LNP™ LUBRICOMP™
Casters、Home appliance components
Thermal stability、UV resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE SINGAPHORE/EFL34HL-BK8065 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 32 kJ/m² |
| Multi axis Instrumented Impact Energy | ISO 6603-2 | 2.65 J | |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 21 kJ/m² |
| Dart impact | 23°C,EnergyatPeakLoad | ASTM D3763 | 8.60 J |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE SINGAPHORE/EFL34HL-BK8065 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 7400 Mpa | |
| ASTM D638 | 7580 Mpa | ||
| elongation | 断裂 | ASTM D638 | 2.2 % |
| bending strength | ISO 178 | 181 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 2.2 % |
| Flexural modulus | ISO 178 | 7950 Mpa | |
| bending strength | ASTM D790 | 179 Mpa | |
| tensile strength | 断裂 | ASTM D638 | 113 Mpa |
| 断裂 | ISO 527-2 | 113 Mpa | |
| Flexural modulus | ASTM D790 | 7520 Mpa |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE SINGAPHORE/EFL34HL-BK8065 |
|---|---|---|---|
| Shrinkage rate | MD:24小时 | ISO 294-4 | 0.33 % |
| MD：24小时 | ASTM D955 | 0.30 % | |
| Water absorption rate | 24hr,50%RH | ASTM D570 | 0.17 % |
| 平衡,23°C,50%RH | ISO 62 | 0.23 % | |
| Shrinkage rate | TD：24hr | ASTM D955 | 0.60 % |
| TD:24小时 | ISO 294-4 | 0.60 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE SINGAPHORE/EFL34HL-BK8065 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,64.0mm跨距，HDT | ISO 75-2/Af | 204 °C |
| 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 203 °C |