برگه داده فنی مقایسهimpact performance شرایط آزمون روش آزمون نتیجه آزمون Impact strength of cantilever beam gap 23°C, 6.40 mm, Injection ASTM D256 49 J/m
flammability شرایط آزمون روش آزمون نتیجه آزمون UL flame retardant rating 0.70 mm UL 94 V-2
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون bending strength 23°C, 3.20 mm, Injection ASTM D790 102 Mpa Bending modulus 23°C, 3.20 mm, Injection ASTM D790 2550 Mpa elongation Break, 23°C, 3.20 mm, Injection ASTM D638 > 40 % tensile strength Break, 23°C, 3.20 mm, Injection ASTM D638 74.5 Mpa
injection شرایط آزمون روش آزمون نتیجه آزمون Mold temperature 60 to 90 °C Processing (melt) temperature 260 to 280 °C Spray nozzle temperature 260 to 280 °C Temperature at the front of the material cylinder 260 to 275 °C Temperature in the middle of the barrel 260 to 275 °C Temperature at the rear of the barrel 255 to 270 °C Suggested maximum moisture content 0.10 % drying time 4.0 to 5.0 hr drying temperature 80 to 100 °C
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Melting temperature ASTM D3418 260 °C Hot deformation temperature 1.8 MPa, Unannealed, 6.40 mm, Injection ASTM D648 75.0 °C Hot deformation temperature 0.45 MPa, Unannealed, 6.40 mm, Injection ASTM D648 230 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Water absorption rate 24 hr, 23°C ASTM D570 1.7 % Shrinkage rate 23°C, Injection,Flow ASTM D955 1.3 - 2.0 % density ASTM D792 1.14 g/cm³