PA66 GP1000BG LG GUANGZHOU
LUMID®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | LG GUANGZHOU/GP1000BG |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C, 6.40 mm, 注塑 | ASTM D256 | 49 J/m |
| Mechanical properties | Test Condition | Test Method | LG GUANGZHOU/GP1000BG |
|---|---|---|---|
| tensile strength | 断裂, 23°C, 3.20 mm, 注塑 | ASTM D638 | 74.5 Mpa |
| bending strength | 23°C, 3.20 mm, 注塑 | ASTM D790 | 102 Mpa |
| Flexural modulus | 23°C, 3.20 mm, 注塑 | ASTM D790 | 2550 Mpa |
| elongation | 断裂, 23°C, 3.20 mm, 注塑 | ASTM D638 | > 40 % |
| flammability | Test Condition | Test Method | LG GUANGZHOU/GP1000BG |
|---|---|---|---|
| UL flame retardant rating | 0.70 mm | UL 94 | V-2 |
| physical property | Test Condition | Test Method | LG GUANGZHOU/GP1000BG |
|---|---|---|---|
| Shrinkage rate | 23°C, 注塑，Flow | ASTM D955 | 1.3 - 2.0 % |
| Water absorption rate | 24 hr, 23°C | ASTM D570 | 1.7 % |
| density | ASTM D792 | 1.14 g/cm³ |
| Thermal performance | Test Condition | Test Method | LG GUANGZHOU/GP1000BG |
|---|---|---|---|
| Heat distortion temperature | 1.8 MPa, 未退火, 6.40 mm, 注塑，HDT | ASTM D648 | 75.0 °C |
| melting temperature | ASTM D3418 | 260 °C | |
| Heat distortion temperature | 0.45 MPa, 未退火, 6.40 mm, 注塑，HDT | ASTM D648 | 230 °C |
| injection | Test Condition | Test Method | LG GUANGZHOU/GP1000BG |
|---|---|---|---|
| drying time | 4.0 to 5.0 hr | ||
| Suggested maximum moisture content | 0.10 % | ||
| Temperature in the middle of the barrel | 260 to 275 °C | ||
| Temperature at the rear of the barrel | 255 to 270 °C | ||
| Processing (melt) temperature | 260 to 280 °C | ||
| drying temperature | 80 to 100 °C | ||
| Temperature at the front of the material cylinder | 260 to 275 °C | ||
| Temperature | 60 to 90 °C | ||
| Spray nozzle temperature | 260 to 280 °C |