Impact strength of simply supported beam without notch
-30°C
ISO 179
65 kJ/m²
Impact strength of simply supported beam without notch
23°C
ISO 179
80 kJ/m²
Impact strength of cantilever beam gap
-40°C
ASTM D256
110 J/m
Impact strength of cantilever beam gap
23°C
ASTM D256
150 J/m
Impact strength of cantilever beam gap
23°C
ISO 180
12 kJ/m²
mechanical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
Tensile modulus
23°C
ISO 527-2
9500 Mpa
tensile strength
Break,23°C
ASTM D638
180 Mpa
tensile strength
Break,23°C
ISO 527-2
180 Mpa
Tensile strain
Break,23°C
ISO 527-2
3.0 %
Bending modulus
23°C
ISO 178
8300 Mpa
thermal performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Hot deformation temperature
0.45MPa,Unannealed
ASTM D648
220 °C
Hot deformation temperature
0.45MPa,Unannealed
ISO 75-2/B
220 °C
Hot deformation temperature
1.8MPa,Unannealed
ASTM D648
210 °C
Hot deformation temperature
1.8MPa,Unannealed
ISO 75-2/A
205 °C
Melting temperature
ASTM D3418
220 °C
Melting temperature
ISO 3146
220 °C
Physical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
density
ASTM D792
1.36 g/cm³
density
ISO 1183
1.36 g/cm³
Melt Volume Flow Rate (MVR)
275°C/5.0kg
ISO 1133
40.0 cm3/10min
Shrinkage rate
MD:3.18mm
0.30 %
Water absorption rate
Saturation
ASTM D570
6.6 %
Water absorption rate
Saturation,23°C
ISO 62
6.6 %
Water absorption rate
Equilibrium,50%RH
ASTM D570
2.1 %
Water absorption rate
Equilibrium,23°C,50%RH
ISO 62
2.1 %
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.