Material Comparison

Product Info

Product Name

Brand Name

Usages

Properties

Certificates

PA6 B3WG6GP BASF GERMANY

Ultramid®

Automotive sector,Engine hood parts,Application in the automotive field

Thermal stability,Oil resistant,Filler: Glass fiber reinf,30% filler by weight

Plastic Datasheets

thermal performance	Test Condition	Test Method	BASF GERMANY/B3WG6GP
Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	210 °C
		0.45MPa,Unannealed	ISO 75-2/B	220 °C
		1.8MPa,Unannealed	ISO 75-2/A	205 °C
		0.45MPa,Unannealed	ASTM D648	220 °C
Melting temperature		ASTM D3418	220 °C
Melting temperature			ISO 3146	220 °C

mechanical properties	Test Condition	Test Method	BASF GERMANY/B3WG6GP
Bending modulus	23°C	ISO 178	8300 Mpa
Tensile modulus	23°C	ISO 527-2	9500 Mpa
Tensile strain	Break,23°C	ISO 527-2	3.0 %
tensile strength	Break,23°C	ISO 527-2	180 Mpa
tensile strength		Break,23°C	ASTM D638	180 Mpa

Physical properties	Test Condition	Test Method	BASF GERMANY/B3WG6GP
density		ISO 1183	1.36 g/cm³
density			ASTM D792	1.36 g/cm³
Melt Volume Flow Rate (MVR)	275°C/5.0kg	ISO 1133	40.0 cm3/10min
Shrinkage rate	MD：3.18mm		0.30 %
Water absorption rate	Saturation	ASTM D570	6.6 %
		Equilibrium,23°C,50%RH	ISO 62	2.1 %
		Equilibrium,50%RH	ASTM D570	2.1 %
		Saturation,23°C	ISO 62	6.6 %

impact performance	Test Condition	Test Method	BASF GERMANY/B3WG6GP
Charpy Notched Impact Strength	-30°C	ISO 179	9.0 kJ/m²
Charpy Notched Impact Strength		23°C	ISO 179	12 kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180	12 kJ/m²
		23°C	ASTM D256	150 J/m
		-40°C	ASTM D256	110 J/m
Impact strength of simply supported beam without notch	-30°C	ISO 179	65 kJ/m²
Impact strength of simply supported beam without notch		23°C	ISO 179	80 kJ/m²