physical property	شرایط آزمون	روش آزمون	نتیجه آزمون
Disassembly rate			1.569
Shrinkage rate			0.3-0.7 %
Melting temperature range for pipeline extrusion			220-240 °C
Water absorption rate			0.2 %
melt mass-flow rate	200/21 6		12
melt mass-flow rate	melt mass-flow rate	220/10		10
Melting temperature range for injection molding			220-270 °C
Mold temperature range			40-80 °C

Mechanical properties	شرایط آزمون	نتیجه آزمون
Charpy Notched Impact Strength	23℃	2 KJ/m
Rockwell hardness		83 M
Impact strength of cantilever beam gap	23℃	2 KJ/m
ball-indentation hardness		165 Mpa
Breaking stress		75 Mpa
Tensile stress	屈服	125 Mpa
elongation		3 %
Tensile modulus		3800 Mpa
Charpy Notched Impact Strength	+23/-40℃	18/18 KJ/m
Tensile creep modulus	1000h 伸长率＜＝0.5%+23℃	2800 Mpa

Electrical performance	شرایط آزمون	نتیجه آزمون
Relative Arc Track Index CTI Test Solution	试验溶液A/CTIM	CTI 425
dielectric constant	100Hz/1MHz	3/2.7
Volume resistivity		10 Ω.cm
Surface Resistivity		10 Ω
Relative Arc Track Index CTI Test Solution	试验溶液B	CTI 200M
dielectric strength	K20/P20	95 KV/mm
loss angle	100Hz/1MHz	0.004/0.007

Thermal performance	شرایط آزمون	نتیجه آزمون
Heat distortion temperature	0.45MPa(HDT B)	102 °C
maximum service temperature		85 °C
Heat distortion temperature	1.8MPa(HDT A)	98 °C
Conductivity		0.17 W/K.m
Linear coefficient of thermal expansion	纵向(23-80)℃	7
vicat		106 °C