برگه داده فنی مقایسهBasic Performance شرایط آزمون روش آزمون نتیجه آزمون Water absorption rate ASTM D-570 0.22 %
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون elongation ASTM D-638 70 % Linear coefficient of thermal expansion ASTM D-695 10×0.000001 mm/mm/ºC tension ASTM D-638 625 kg/cm Squeezing coefficient 静 ASTM D-1894 0.12 Squeezing coefficient 动 ASTM D-1894 0.16 Rockwell hardness ASTM D-785 82 M(R) Bending modulus ASTM D-790 26500 kg/cm Impact strength of cantilever beam gap Notched ASTM D-256 7.0 kg.cm/cm Impact strength of cantilever beam gap Unnotched ASTM D-256 80.0 kg.cm/cm bending strength ASTM D-790 1000 kg/cm
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature 4.6kg/cm ASTM D-648 160 ºC Hot deformation temperature 18kg/cm ASTM D-648 110 ºC Combustibility 1/32" HB
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Taber wear resistance ASTM D-1044 14 mg/1000cycles Shrinkage rate 18-22 cm/cm×0.0001 density ASTM D-792 1.41
Electrical performance شرایط آزمون روش آزمون نتیجه آزمون Dielectric constant ASTM D-150 3.8 Dielectric strength ASTM D-149 24 KV/mm Surface resistance ASTM D-257 1×10 Ω Induced positive connection ASTM D-150 0.007 Arc resistance ASTM D-495 240 sec Antibody accumulation ASTM D-257 1×10 Ω.cm
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.