PPS LNP™ THERMOCOMP™  OFL-4036 SABIC INNOVATIVE US

245
  • Unit Price:US$ 6,050 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    25.7MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:Flame retardant｜High heat resistance｜Filler: Glass fiber reinforced material｜30% filler by weight
  • Application Areas:Electronic and electrical components
  • Color:--
  • Grade:Injection grade

Technical Data Sheet

impact performanceTest ConditionTest MethodTest Result
Dart impact23°C,TotalEnergyASTM D376311.8 J
Multi axis Instrumented Impact EnergyISO 6603-22.30 J
Impact strength of cantilever beam gap23°CISO 180/1A5.7 kJ/m²
Suspended wall beam without notch impact strength23°CISO 180/1U25 kJ/m²
Dart impact23°C,EnergyatPeakLoadASTM D37633.40 J
mechanical propertiesTest ConditionTest MethodTest Result
bending strengthBreak,50.0mmSpanASTM D790178 Mpa
Friction coefficientDynamicASTM D3702Modified0.44
Friction coefficientStaticASTM D3702Modified0.35
Wear factorRingASTM D3702Modified7.00to8.00 10^-10in^5-min/ft-lb-hr
Wear factorWasherASTM D3702Modified52.5 10^-10in^5-min/ft-lb-hr
Tensile modulusASTM D63812800 Mpa
Tensile modulusISO 527-2/112000 Mpa
tensile strengthBreakASTM D638124 Mpa
tensile strengthBreakISO 527-2/5121 Mpa
elongationBreakASTM D6381.3 %
Tensile strainBreakISO 527-2/51.3 %
Bending modulus50.0mmSpanASTM D79011600 Mpa
Bending modulusISO 17811100 Mpa
bending strengthISO 178180 Mpa
thermal performanceTest ConditionTest MethodTest Result
Hot deformation temperature0.45MPa,Unannealed,3.20mmASTM D648278 °C
Hot deformation temperature0.45MPa,Unannealed,64.0mmSpanISO 75-2/Bf278 °C
Hot deformation temperature1.8MPa,Unannealed,3.20mmASTM D648264 °C
Hot deformation temperature1.8MPa,Unannealed,64.0mmSpanISO 75-2/Af257 °C
Linear coefficient of thermal expansionMD：-30to30°CASTM D6962.5E-05 cm/cm/°C
Linear coefficient of thermal expansionMD：-40to40°CASTME8312.3E-5to5.0E-5 cm/cm/°C
Linear coefficient of thermal expansionMD：-40to40°CISO 11359-22.4E-05 cm/cm/°C
Linear coefficient of thermal expansionTD：-30to30°CASTM D6963.4E-05 cm/cm/°C
Linear coefficient of thermal expansionTD：-40to40°CASTME8314.9E-05 cm/cm/°C
Linear coefficient of thermal expansionTD：-40to40°CISO 11359-25E-05 cm/cm/°C
Physical propertiesTest ConditionTest MethodTest Result
Shrinkage rateMD：24hrASTM D9550.10-0.20 %
Shrinkage rateTD：24hrASTM D9550.60-0.80 %
Shrinkage rateTD:24hrISO 294-40.30-0.48 %
Shrinkage rateMD:24hrISO 294-40.13-0.18 %
Water absorption rate24hr,50%RHASTM D5701.2E-03 %
Water absorption rateEquilibrium,23°C,50%RHISO 620.010 %
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.