PC/ABS

PC/ABS CYCOLOY™ CX7211 8T5D007U SABIC INNOVATIVE NANSHA

Unit Price:US$ 4,421 /MT
Packaging Specification:
Supply Quantity:
10MT
Delivery Terms:
DDP
:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Low temperature resistance｜High sliding
Application Areas:Electronic and electrical accessories｜Automotive components
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	10 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	40 kJ/m²
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	10 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	40 kJ/m²
Dart impact	23°C,TotalEnergy	ASTM D3763	60.0 J

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.3mm	UL 94	V-1
	UL flame retardant rating	1.5mm	UL 94	V-0
		UL flame retardant rating	2.0mm	UL 94	5VB
		UL flame retardant rating	UL flame retardant rating	2.5mm	UL 94	5VA
Burning wire flammability index	1.0mm	IEC 60695-2-12	960 °C
Hot filament ignition temperature	1.0mm	IEC 60695-2-13	800 °C
Hot filament ignition temperature	Hot filament ignition temperature	3.0mm	IEC 60695-2-13	800 °C
Extreme Oxygen Index		ISO 4589-2	32 %

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ASTM D638	2950 Mpa
Tensile modulus	Tensile modulus		ISO 527-2/1	2800 Mpa
tensile strength	Yield	ASTM D638	66.0 Mpa
	tensile strength	Yield	ISO 527-2/50	62.0 Mpa
		tensile strength	Break	ASTM D638	60.0 Mpa
		tensile strength	tensile strength	Break	ISO 527-2/50	55.0 Mpa
elongation	Yield	ASTM D638	4.0 %
Tensile strain	Yield	ISO 527-2/50	4.0 %
elongation	Break	ASTM D638	98 %
Tensile strain	Break	ISO 527-2/50	90 %
Bending modulus	50.0mmSpan	ASTM D790	2750 Mpa
Bending modulus	Bending modulus		ISO 178	2500 Mpa
bending strength		ISO 178	100 Mpa
bending strength	bending strength	Yield,50.0mmSpan	ASTM D790	103 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed,6.40mm	ASTM D648	102 °C
	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	89.0 °C
		Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	96.0 °C
		Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	90.0 °C
Vicat softening temperature		ASTM D152510	105 °C
	Vicat softening temperature	--	ISO 306/B50	105 °C
	Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	105 °C
Ball Pressure Test	75°C	IEC 60695-10-2	Pass
Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	6.1E-05 cm/cm/°C
	Linear coefficient of thermal expansion	MD：-40to40°C	ISO 11359-2	7.5E-05 cm/cm/°C
		Linear coefficient of thermal expansion	TD：-40to40°C	ASTME831	5.5E-05 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：-40to40°C	ISO 11359-2	7.5E-05 cm/cm/°C
thermal conductivity		ISO 8302	0.20 W/m/K
RTI Elec		UL 746	90.0 °C
RTI Imp		UL 746	90.0 °C
RTI Str		UL 746	90.0 °C
Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	94.0 °C

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	260°C/2.16kg	ASTM D1238	16 g/10min
Melt Volume Flow Rate (MVR)	260°C/2.16kg	ISO 1133	14.0 cm3/10min
Shrinkage rate	MD：3.20mm	Internal Method	0.40-0.60 %
Water absorption rate	Saturation,23°C	ISO 62	0.24 %
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.12 %

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		IEC 60093	>1.0E+15 ohms
Volume resistivity		IEC 60093	>1.0E+15 ohms·cm
Dielectric strength	0.800mm,in Oil	IEC 60243-1	35 KV/mm
	Dielectric strength	1.60mm,in Oil	IEC 60243-1	25 KV/mm
	Dielectric strength	Dielectric strength	3.20mm,in Oil	IEC 60243-1	17 KV/mm
Compared to the anti leakage trace index	CTI	UL 746	PLC 3
High arc combustion index	HAI	UL 746	PLC 0
Hot wire ignition	HWI	UL 746	PLC 2

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.