PC/ABS CX7211 8T5D007U SABIC INNOVATIVE NANSHA

CYCOLOY™

Electronic and electrical accessories,Automotive components

Low temperature resistanc,High sliding

--

--

--

--

--

--

--

--

--

--

--

--

--

--

--

Plastic Datasheets

thermal performance	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/CX7211 8T5D007U
Ball Pressure Test	75°C	IEC 60695-10-2	Pass
Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	89.0 °C
		1.8MPa,Unannealed,6.40mm	ASTM D648	96.0 °C
		1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	90.0 °C
		0.45MPa,Unannealed,3.20mm	ASTM D648	94.0 °C
		0.45MPa,Unannealed,6.40mm	ASTM D648	102 °C
Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	6.1E-05 cm/cm/°C
		TD：-40to40°C	ISO 11359-2	7.5E-05 cm/cm/°C
		TD：-40to40°C	ASTME831	5.5E-05 cm/cm/°C
		MD：-40to40°C	ISO 11359-2	7.5E-05 cm/cm/°C
RTI Elec		UL 746	90.0 °C
RTI Imp		UL 746	90.0 °C
RTI Str		UL 746	90.0 °C
thermal conductivity		ISO 8302	0.20 W/m/K
Vicat softening temperature	--	ISO 306/B120	105 °C
		--	ISO 306/B50	105 °C
			ASTM D152510	105 °C

mechanical properties	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/CX7211 8T5D007U
Bending modulus	50.0mmSpan	ASTM D790	2750 Mpa
Bending modulus			ISO 178	2500 Mpa
bending strength	Yield,50.0mmSpan	ASTM D790	103 Mpa
bending strength			ISO 178	100 Mpa
elongation	Break	ASTM D638	98 %
elongation		Yield	ASTM D638	4.0 %
Tensile modulus		ASTM D638	2950 Mpa
Tensile modulus			ISO 527-2/1	2800 Mpa
Tensile strain	Break	ISO 527-2/50	90 %
Tensile strain		Yield	ISO 527-2/50	4.0 %
tensile strength	Yield	ASTM D638	66.0 Mpa
		Yield	ISO 527-2/50	62.0 Mpa
		Break	ISO 527-2/50	55.0 Mpa
		Break	ASTM D638	60.0 Mpa

Electrical performance	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/CX7211 8T5D007U
Compared to the anti leakage trace index	CTI	UL 746	PLC 3
Dielectric strength	3.20mm,in Oil	IEC 60243-1	17 KV/mm
		1.60mm,in Oil	IEC 60243-1	25 KV/mm
		0.800mm,in Oil	IEC 60243-1	35 KV/mm
High arc combustion index	HAI	UL 746	PLC 0
Hot wire ignition	HWI	UL 746	PLC 2
Surface resistivity		IEC 60093	>1.0E+15 ohms
Volume resistivity		IEC 60093	>1.0E+15 ohms·cm

Physical properties	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/CX7211 8T5D007U
melt mass-flow rate	260°C/2.16kg	ASTM D1238	16 g/10min
Melt Volume Flow Rate (MVR)	260°C/2.16kg	ISO 1133	14.0 cm3/10min
Shrinkage rate	MD：3.20mm	Internal Method	0.40-0.60 %
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.12 %
Water absorption rate		Saturation,23°C	ISO 62	0.24 %

impact performance	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/CX7211 8T5D007U
Charpy Notched Impact Strength	23°C	ISO 179/1eA	40 kJ/m²
Charpy Notched Impact Strength		-30°C	ISO 179/1eA	10 kJ/m²
Dart impact	23°C,TotalEnergy	ASTM D3763	60.0 J
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	10 kJ/m²
Impact strength of cantilever beam gap		23°C	ISO 180/1A	40 kJ/m²

flammability	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/CX7211 8T5D007U
Burning wire flammability index	1.0mm	IEC 60695-2-12	960 °C
Extreme Oxygen Index		ISO 4589-2	32 %
Hot filament ignition temperature	3.0mm	IEC 60695-2-13	800 °C
Hot filament ignition temperature		1.0mm	IEC 60695-2-13	800 °C
UL flame retardant rating	2.5mm	UL 94	5VA
		2.0mm	UL 94	5VB
		1.3mm	UL 94	V-1
		1.5mm	UL 94	V-0