| 弹性体 | 测试条件 | 测试方法 | 测试结果 |
|---|---|---|---|
| 伸长率 | 断裂,23°C，横向 | ASTM D412 | 600 % |
| 断裂,23°C，横向 | ISO 37 | 600 % | |
| 压缩永久变形 | 125°C,70hr | ASTM D395B | 55 % |
| 125°C,70hr | ISO 815 | 55 % |
| 硬度 | 测试条件 | 测试方法 | 测试结果 |
|---|---|---|---|
| 邵氏硬度 | 邵氏A,15秒,23°C | ISO 868 | 53 |
| 老化 | 测试条件 | 测试方法 | 测试结果 |
|---|---|---|---|
| 空气中拉伸强度的变化率 | 100°C,168hr | ASTM D573 | -28 % |
| 125°C,168hr | ASTM D573 | -61 % | |
| 100°C,168hr | ISO 188 | -28 % | |
| 125°C,168hr | ISO 188 | -61 % | |
| 空气中硬度(Shore)的变化率 | ShoreA,23°C,168hr,inIRM903Oil | ASTM D471 | -33 |
| ShoreA,23°C,168hr,inSodiumHydroxide,50% | ASTM D471 | 4.0 | |
| ShoreA,23°C,168hr,inWater | ASTM D471 | 5.0 | |
| 邵氏硬度 | ShoreA,23°C,168hr,inEthanol,95% | ISO 1817 | 2.0 |
| ShoreA,23°C,168hr,inHydrochloricAcid,10% | ISO 1817 | 4.0 | |
| ShoreA,23°C,168hr,inIRM903Oil | ISO 1817 | -33 | |
| ShoreA,23°C,168hr,inSodiumHydroxide,50% | ISO 1817 | 4.0 | |
| ShoreA,23°C,168hr,inWater | ISO 1817 | 5.0 | |
| 空气中极限伸长率的变化率 | 100°C,168hr | ASTM D573 | -14 % |
| 125°C,168hr | ASTM D573 | -70 % | |
| 拉伸应力变化率 | 100°C,168hr，断裂 | ISO 188 | -14 % |
| 125°C,168hr，断裂 | ISO 188 | -70 % | |
| 空气中硬度(Shore)的变化率 | ShoreA,100°C,168hr | ASTM D573 | -4.0 |
| 邵氏A,125°C,168hr | ASTM D573 | 8.0 | |
| ShoreA,100°C,168hr | ISO 188 | -4.0 | |
| 邵氏A,125°C,168hr | ISO 188 | 8.0 | |
| 空气中拉伸强度的变化率 | 23°C,168hr,inEthanol,95% | ASTM D471 | -17 % |
| 23°C,168hr,inHydrochloricAcid,10% | ASTM D471 | -1.0 % | |
| 空气中极限伸长率的变化率 | 23°C,168hr,inIRM903Oil | ASTM D471 | -68 % |
| 23°C,168hr,inSodiumHydroxide,50% | ASTM D471 | -7.0 % | |
| 23°C,168hr,在水中 | ASTM D471 | -12 % | |
| 拉伸应力变化率 | 23°C,168hr,inEthanol,95%，断裂 | ISO 1817 | -3.0 % |
| 23°C,168hr,inHydrochloricAcid,10%，断裂 | ISO 1817 | -9.0 % | |
| 23°C,168hr,inIRM903Oil，断裂 | ISO 1817 | -68 % | |
| 23°C,168hr,inSodiumHydroxide,50%，断裂 | ISO 1817 | -7.0 % | |
| 23°C,168hr,在水中，断裂 | ISO 1817 | -12 % | |
| 空气中硬度(Shore)的变化率 | ShoreA,23°C,168hr,inEthanol,95% | ASTM D471 | 2.0 |
| ShoreA,23°C,168hr,inHydrochloricAcid,10% | ASTM D471 | 4.0 | |
| 空气中拉伸强度的变化率 | 23°C,168hr,inIRM903Oil | ASTM D471 | -85 % |
| 23°C,168hr,inSodiumHydroxide,50% | ASTM D471 | 1.0 % | |
| 23°C,168hr,在水中 | ASTM D471 | 2.0 % | |
| 23°C,168hr,inEthanol,95% | ISO 1817 | -17 % | |
| 23°C,168hr,inHydrochloricAcid,10% | ISO 1817 | -1.0 % | |
| 23°C,168hr,inIRM903Oil | ISO 1817 | -85 % | |
| 23°C,168hr,inSodiumHydroxide,50% | ISO 1817 | 1.0 % | |
| 23°C,168hr,在水中 | ISO 1817 | 2.0 % | |
| 空气中极限伸长率的变化率 | 23°C,168hr,inEthanol,95% | ASTM D471 | -3.0 % |
| 23°C,168hr,inHydrochloricAcid,10% | ASTM D471 | -9.0 % |
| 可燃性 | 测试条件 | 测试方法 | 测试结果 |
|---|---|---|---|
| UL阻燃等级 | 1.1mm | UL 94 | HB |
| 2.9mm | UL 94 | HB |