Fluorelastomer Viton® A-331C
0
比对物性数据
| 物理性能 | 测试条件 | 测试方法 | 测试结果 |
|---|---|---|---|
| 密度 | ASTM D792 | 1.82 g/cm³ | |
| 表观密度 | ASTM D1895 | 1.82 g/cm³ | |
| 门尼粘度 | ML1+10,121°C | ASTM D1646 | 65 MU |
| 弹性体 | 测试条件 | 测试方法 | 测试结果 |
|---|---|---|---|
| 拉伸强度 | 100%应变,23°C8 | ASTM D412 | 4.50 MPa |
| 100%应变,23°C9 | ASTM D412 | 4.50 MPa | |
| 100%应变,23°C6 | ASTM D412 | 3.10 MPa | |
| 100%应变,23°C7 | ASTM D412 | 4.60 MPa | |
| 伸长率 | 断裂,23°C10 | ASTM D412 | 230 % |
| 压缩永久变形 | 23°C,70hr | ASTM D395B | 18 % |
| 200°C,70hr | ASTM D395B | 21 % | |
| 200°C,168hr | ASTM D395B | 29 % | |
| 232°C,70hr | ASTM D395B | 40 % | |
| 拉伸强度 | 100%应变,23°C10 | ASTM D412 | 4.90 MPa |
| 屈服,23°C6 | ASTM D412 | 9.70 MPa | |
| 屈服,23°C7 | ASTM D412 | 14.5 MPa | |
| 屈服,23°C8 | ASTM D412 | 15.0 MPa | |
| 屈服,23°C9 | ASTM D412 | 13.5 MPa | |
| 屈服,23°C10 | ASTM D412 | 14.1 MPa | |
| 伸长率 | 断裂,23°C6 | ASTM D412 | 350 % |
| 断裂,23°C7 | ASTM D412 | 240 % | |
| 断裂,23°C8 | ASTM D412 | 260 % | |
| 断裂,23°C9 | ASTM D412 | 240 % |
| 硬度 | 测试条件 | 测试方法 | 测试结果 |
|---|---|---|---|
| 邵氏硬度 | 邵氏A,23°C2 | ASTM D2240 | 75 |
| 邵氏A,23°C3 | ASTM D2240 | 72 | |
| 邵氏A,23°C4 | ASTM D2240 | 77 | |
| 邵氏A,23°C5 | ASTM D2240 | 76 | |
| 邵氏A,23°C | ASTM D2240 | 71 |