Ethylene Copolymer Teflon® PFA 940HP Plus
0
- 特性:热性能
比对物性数据
| 测试条件 | 测试方法 | 测试结果 | |
|---|---|---|---|
| 熔融温度 | ASTM D4591 | 290 °C | |
| 体积电阻率 | ASTM D257 | 1E+18 ohms·cm | |
| ISO 1325 | 1E+18 ohms·cm | ||
| 介电强度 | 0.250mm | ASTM D149 | 80 kV/mm |
| 0.250mm | IEC 60243-1 | 80 kV/mm | |
| 介电常数 | 1MHz | ASTM D150 | 2.03 |
| 1MHz | IEC 60250 | 2.03 | |
| 耗散因数 | 1MHz | ASTM D150 | <2.0E-4 |
| 邵氏硬度 | 邵氏D | ASTM D2240 | 55 |
| 邵氏D | ISO 868 | 55 | |
| 拉伸强度 | 200°C | ISO 12086 | 11.0 MPa |
| 伸长率 | 断裂,23°C | ASTM D3307 | 310 % |
| 断裂,200°C | ASTM D3307 | 450 % | |
| 拉伸应变 | 断裂,23°C | ISO 12086 | 310 % |
| 断裂,200°C | ISO 12086 | 450 % | |
| 弯曲模量 | 23°C | ASTM D790 | 650 MPa |
| 200°C | ASTM D790 | 60.0 MPa | |
| 23°C | ISO 178 | 650 MPa | |
| 200°C | ISO 178 | 60.0 MPa | |
| 耗散因数 | 1MHz | IEC 60250 | <2.0E-4 |
| UL阻燃等级 | UL 94 | V-0 | |
| 极限氧指数 | ASTM D2863 | >95 % | |
| ISO 4589-2 | >95 % | ||
| 临界剪切速率 | 372°C | 56.0 sec^-1 | |
| MITFoldingEndurance | 200.0µm | ASTM D2176 | 3E+05 Cycles |
| 拉伸强度 | 23°C | ISO 12086 | 28.0 MPa |
| 密度 | ASTM D792 | 2.14 g/cm³ | |
| 熔体质量流动速率 | 372°C/5.0kg | ASTM D3307 | 16 g/10min |
| 372°C/5.0kg | ISO 12086 | 16 g/10min | |
| 吸水率 | 24hr | ASTM D570 | <0.030 % |
| 拉伸强度 | 23°C | ASTM D3307 | 28.0 MPa |
| 200°C | ASTM D3307 | 11.0 MPa |