MMW-HDPE TOTAL Polyethylene HDPE D4720 法国TOTAL石化
0
比对物性数据
| 物理性能 | 测试条件 | 测试方法 | 测试结果 |
|---|---|---|---|
| 密度 | ASTM D792 | 0.947 g/cm³ | |
| 熔体质量流动速率 | 190°C/2.16kg | ASTM D1238 | 0.28 g/10min |
| 190°C/21.6kg | ASTM D1238 | 20 g/10min |
| 补充信息 | 测试条件 | 测试方法 | 测试结果 |
|---|---|---|---|
| DartImpact | 25.4µm19 | ASTM D1709 | 100 g |
| 热性能 | 测试条件 | 测试方法 | 测试结果 |
|---|---|---|---|
| 熔融温度 | ASTM D3417 | 131 °C |
| 薄膜 | 测试条件 | 测试方法 | 测试结果 |
|---|---|---|---|
| 割线模量 | 1%正割,TD:25µm | ASTM D882A | 1000 MPa |
| 拉伸强度 | MD:屈服,25µm2 | ASTM D882A | 24.1 MPa |
| MD:屈服,25µm3 | ASTM D882A | 23.4 MPa | |
| TD:屈服,25µm4 | ASTM D882A | 25.5 MPa | |
| TD:屈服,25µm5 | ASTM D882A | 26.2 MPa | |
| 伸长率 | MD:断裂,25µm10 | ASTM D882A | 600 % |
| MD:断裂,25µm11 | ASTM D882A | 450 % | |
| TD:断裂,25µm12 | ASTM D882A | 700 % | |
| TD:断裂,25µm13 | ASTM D882A | 600 % | |
| 埃尔曼多夫撕裂强度 | MD:25µm14 | ASTM D1922 | 28 g |
| MD:25µm15 | ASTM D1922 | 10 g | |
| TD:25µm16 | ASTM D1922 | 530 g | |
| TD:25µm17 | ASTM D1922 | 1500 g | |
| 水蒸气透过率 | 38°C,25µm | ASTME96 | 7.8 g/m²/24hr |
| 薄膜厚度 | 25 µm | ||
| 割线模量 | 1%正割,MD:25µm | ASTM D882A | 710 MPa |
| 拉伸强度 | MD:断裂,25µm6 | ASTM D882A | 4.83 MPa |
| MD:断裂,25µm7 | ASTM D882A | 62.1 MPa | |
| TD:断裂,25µm8 | ASTM D882A | 39.3 MPa | |
| TD:断裂,25µm9 | ASTM D882A | 18.6 MPa |
免责声明：此数据表中的信息由 Plas.Com 从该材料的生产商或第三方处获得。Plas.Com 尽最大努力确保此数据的准确性。 但是 Plas.Com 对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。