物性数据
| 物理性能 | 测试条件 | 测试方法 | 测试结果 |
|---|
| 密度 | --2 | ASTM D792 | 1.35 g/cm³ |
| 密度 | --3 | ASTM D792 | 1.36 g/cm³ |
| 吸水率 | 24hr,1.57mm | ASTM D570 | 2.0 % |
| 吸水率 | 24hr,3.18mm | ASTM D570 | 1.2 % |
| 吸水率 | 24hr,12.7mm | ASTM D570 | 0.74 % |
| 补充信息 | 测试条件 | 测试方法 | 测试结果 |
|---|
| 粘度 | 1.27cm | ASTM D229 | 880000 g |
| 热性能 | 测试条件 | 测试方法 | 测试结果 |
|---|
| 线性热膨胀系数 | MD:3.18mm | | 2.6E-05 cm/cm/°C |
| 线性热膨胀系数 | TD:3.18mm | | 2.2E-05 cm/cm/°C |
| 可燃性 | 测试条件 | 测试方法 | 测试结果 |
|---|
| UL阻燃等级 | 1.6mm | UL 94 | HB |
| UL阻燃等级 | 3.2mm | UL 94 | HB |
| UL阻燃等级 | 12.7mm | UL 94 | V-0 |
| 电气性能 | 测试条件 | 测试方法 | 测试结果 |
|---|
| 耗散因数 | 1.57mm,60Hz | ASTM D150 | 0.22 |
| 耗散因数 | 1.57mm,1kHz | ASTM D150 | 0.79 |
| 耗散因数 | 1.57mm,1MHz | ASTM D150 | 0.043 |
| 耗散因数 | 3.18mm,60Hz | ASTM D150 | 0.27 |
| 耗散因数 | 3.18mm,1kHz | ASTM D150 | 0.093 |
| 耗散因数 | 3.18mm,1MHz | ASTM D150 | 0.046 |
| 耐电弧性 | 1.57mm | ASTM D495 | 143 sec |
| 耐电弧性 | 3.18mm | ASTM D495 | 148 sec |
| 耐电弧性 | 12.7mm | ASTM D495 | 63.0 sec |
| 介电强度 | 1.57mm | ASTM D149 | 83000 V |
| 介电强度 | 3.18mm | ASTM D149 | 73000 V |
| 介电强度 | 1.27cm | ASTM D149 | 57000 V |
| 表面电阻率 | 1.57mm | ASTM D257 | 2.2E+11 ohms |
| 表面电阻率 | 3.18mm | ASTM D257 | 1.6E+12 ohms |
| 体积电阻率 | 1.57mm | ASTM D257 | 4.4E+10 ohms·cm |
| 体积电阻率 | 3.18mm | ASTM D257 | 1.1E+10 ohms·cm |
| 介电强度 | 1.57mm | ASTM D149 | 17 kV/mm |
| 介电强度 | 3.18mm | ASTM D149 | 14 kV/mm |
| 介电常数 | 1.57mm,60Hz | ASTM D150 | 7.84 |
| 介电常数 | 1.57mm,1kHz | ASTM D150 | 6.81 |
| 介电常数 | 1.57mm,1MHz | ASTM D150 | 5.68 |
| 介电常数 | 3.18mm,60Hz | ASTM D150 | 9.49 |
| 介电常数 | 3.18mm,1kHz | ASTM D150 | 7.56 |
| 介电常数 | 3.18mm,1MHz | ASTM D150 | 6.15 |
| 机械性能 | 测试条件 | 测试方法 | 测试结果 |
|---|
| 压缩强度 | 1.57mm6 | ASTM D695 | 64.1 MPa |
| 压缩强度 | 1.57mm7 | ASTM D695 | 63.4 MPa |
| 压缩强度 | 3.18mm6 | ASTM D695 | 173 MPa |
| 压缩强度 | 3.18mm7 | ASTM D695 | 170 MPa |
| 压缩强度 | 3.18mm8 | ASTM D695 | >310 MPa |
| 拉伸强度 | 流量:1.57mm | ASTM D638 | 88.9 MPa |
| 压缩强度 | 12.7mm6 | ASTM D695 | 84.8 MPa |
| 压缩强度 | 12.7mm8 | ASTM D695 | >310 MPa |
| 弯曲强度 | 1.57mm5 | ASTM D790 | 110 MPa |
| 弯曲强度 | 3.18mm4 | ASTM D790 | 122 MPa |
| 弯曲强度 | 3.18mm5 | ASTM D790 | 105 MPa |
| 拉伸强度 | 横向流量:1.57mm | ASTM D638 | 55.8 MPa |
| 拉伸强度 | 流量:3.18mm | ASTM D638 | 93.8 MPa |
| 拉伸强度 | 横向流量:3.18mm | ASTM D638 | 68.9 MPa |
| 弯曲强度 | 1.57mm4 | ASTM D790 | 147 MPa |
| 弯曲强度 | 12.7mm4 | ASTM D790 | 121 MPa |
| 弯曲强度 | 12.7mm5 | ASTM D790 | 99.3 MPa |
| 冲击性能 | 测试条件 | 测试方法 | 测试结果 |
|---|
| 悬壁梁缺口冲击强度 | 横向流量:1.57mm | ASTM D256 | 47 J/m |
| 悬壁梁缺口冲击强度 | 横向流量:3.18mm | ASTM D256 | 46 J/m |
| 悬壁梁缺口冲击强度 | 横向流量:12.7mm | ASTM D256 | 48 J/m |
| 悬壁梁缺口冲击强度 | 流量:1.57mm | ASTM D256 | 65 J/m |
| 悬壁梁缺口冲击强度 | 流量:3.18mm | ASTM D256 | 61 J/m |
| 悬壁梁缺口冲击强度 | 流量:12.7mm | ASTM D256 | 54 J/m |
免责声明：此数据表中的信息由 Plas.Com 从该材料的生产商或第三方处获得。Plas.Com 尽最大努力确保此数据的准确性。 但是 Plas.Com 对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。