物性数据
| 物理性能 | 测试条件 | 测试方法 | 测试结果 |
|---|
| 熔体质量流动速率 | 190°C/2.16kg | ASTM D1238 | 4.0 g/10min |
| 基本性能 | 测试条件 | 测试方法 | 测试结果 |
|---|
| 熔体质量流动速率 | | ASTM D1238 | 4 g/10min |
| 密度 | | ASTM D792 | 0.904 g/cm³ |
| 光学性能 | 测试条件 | 测试方法 | 测试结果 |
|---|
| 透明度 | | ASTM D-1746 | 99 |
| 光泽度 | 45° | ASTM D-2457 | 90 |
| 雾度 | | ASTM D-1003 | 1.8 % |
| 光泽度 | 45°,20.3µm | ASTM D2457 | 92 |
| 光泽度 | 45°,50.8µm | ASTM D2457 | 90 |
| 透明度 | 20.3µm | ASTM D1746 | 99.0 |
| 透明度 | 50.8µm | ASTM D1746 | 99.0 |
| 雾度 | 20.3µm | ASTM D1003 | 0.60 % |
| 雾度 | 50.8µm | ASTM D1003 | 1.8 % |
| 热性能 | 测试条件 | 测试方法 | 测试结果 |
|---|
| 维卡软化温度 | | ASTM D-1525 | 71 °C |
| 维卡软化温度 | | ASTM D1525 | 71.1 °C |
| 熔融温度 | | 内部方法 | 124 °C |
| 薄膜 | 测试条件 | 测试方法 | 测试结果 |
|---|
| 落镖冲击 | 20µm | ASTM D1709B | >850 g |
| 落镖冲击 | 51µm | ASTM D1709B | >850 g |
| 埃尔曼多夫撕裂强度 | MD:20µm | ASTM D1922 | 330 g |
| 埃尔曼多夫撕裂强度 | MD:51µm | ASTM D1922 | 960 g |
| 埃尔曼多夫撕裂强度 | TD:20µm | ASTM D1922 | 500 g |
| 埃尔曼多夫撕裂强度 | TD:51µm | ASTM D1922 | 1100 g |
| 氧气透过率 | 23°C,51µm | ASTM D3985 | 450 cm³·mm/m²/atm/24hr |
| 水蒸气透过率 | 51µm | ASTMF1249 | 0.85 g·mm/m²/atm/24hr |
| 二氧化碳透过率 | 23°C,50.8µm | 内部方法 | 2000 cm³·mm/m²/atm/24hr |
| 薄膜穿刺强度 | 20µm | 内部方法 | 18.9 J/cm³ |
| 薄膜穿刺强度 | 51µm | 内部方法 | 17.5 J/cm³ |
| 割线模量 | 2%正割,MD:20µm | ASTM D882 | 58.8 Mpa |
| 割线模量 | 2%正割,MD:51µm | ASTM D882 | 62.6 Mpa |
| 割线模量 | 2%正割,TD:20µm | ASTM D882 | 64.7 Mpa |
| 割线模量 | 2%正割,TD:51µm | ASTM D882 | 63.0 Mpa |
| 拉伸强度 | MD:屈服,20µm | ASTM D882 | 7.00 Mpa |
| 拉伸强度 | MD:屈服,51µm | ASTM D882 | 6.76 Mpa |
| 拉伸强度 | TD:屈服,20µm | ASTM D882 | 4.92 Mpa |
| 拉伸强度 | TD:屈服,51µm | ASTM D882 | 6.34 Mpa |
| 拉伸强度 | MD:断裂,20µm | ASTM D882 | 36.9 Mpa |
| 拉伸强度 | MD:断裂,51µm | ASTM D882 | 32.6 Mpa |
| 拉伸强度 | TD:断裂,20µm | ASTM D882 | 29.1 Mpa |
| 拉伸强度 | TD:断裂,51µm | ASTM D882 | 32.4 Mpa |
| 伸长率 | MD:断裂,20µm | ASTM D882 | 500 % |
| 伸长率 | MD:断裂,51µm | ASTM D882 | 660 % |
| 伸长率 | TD:断裂,20µm | ASTM D882 | 710 % |
| 伸长率 | TD:断裂,51µm | ASTM D882 | 710 % |
| 机械性能 | 测试条件 | 测试方法 | 测试结果 |
|---|
| 穿刺强度 | | 陶氏企业测试 | 17 J/cm³ |
| 拉伸强度 | 屈服,TD | ASTM D-882 | 5 Mpa |
| 拉伸强度 | 屈服,MD | ASTM D-882 | 7 Mpa |
| 拉伸强度 | TD，断裂 | ASTM D-882 | 32 Mpa |
| 拉伸强度 | MD，断裂 | ASTM D-882 | 33 Mpa |
| 断裂伸长率 | TD | ASTM D-882 | 714 % |
| 断裂伸长率 | MD | ASTM D-882 | 664 % |
| 拉伸模量 | TD，2% Secant | ASTM D-882 | 63 Mpa |
| 拉伸模量 | MD，3% Secant | ASTM D-882 | 63 Mpa |