物性数据
| 物理性能 | 测试条件 | 测试方法 | 测试结果 |
|---|
| 熔体体积流动速率 | 160°C/8.7kg | | 35.0 cm3/10min |
| 弹性体 | 测试条件 | 测试方法 | 测试结果 |
|---|
| TensileSet3 | 200%Strain | ASTMD412 | 8 % |
| TensileSet3 | 200%Strain | DIN53504 | 8 % |
| 拉伸强度4 | 100%Strain,0.635mm | ASTMD412 | 2.34 Mpa |
| 拉伸强度4 | 100%Strain,0.635mm | DIN53504 | 1.40 Mpa |
| 压缩永久变形2 | 23°C,70hr | DIN53517 | 35 % |
| 压缩永久变形2 | 70°C,24hr | DIN53517 | 60 % |
| 巴肖氏弹性 | | ASTMD2632 | 60 % |
| 拉伸强度4 | 300%Strain,0.635mm | ASTMD412 | 4.07 Mpa |
| 拉伸强度4 | 300%Strain,0.635mm | DIN53504 | 2.40 Mpa |
| 拉伸强度4 | Break,0.635mm | ASTMD412 | 7.52 Mpa |
| 拉伸强度4 | Break,0.635mm | DIN53504 | 10.0 Mpa |
| 拉伸应变4 | Break,0.635mm | ASTMD412 | 720 % |
| 拉伸应变4 | Break,0.635mm | DIN53504 | 900 % |
| TearStrength4 | 0.635mm | ASTMD624 | 35.9 kN/m |
| TearStrength4 | 0.635mm | DIN53515 | 25 kN/m |
| 压缩永久变形2 | 23°C,70hr | ASTMD395 | 40 % |
| 压缩永久变形2 | 70°C,24hr | ASTMD395 | 80 % |
| 硬度 | 测试条件 | 测试方法 | 测试结果 |
|---|
| 肖氏硬度 | 邵氏A,注塑 | ASTMD2240 | 56 |
| 肖氏硬度 | 邵氏D,注塑 | ASTMD2240 | 15 |
| 肖氏硬度 | 邵氏A,注塑 | DIN53505 | 55 |
| 肖氏硬度 | 邵氏D,注塑 | DIN53505 | 15 |
| 热性能 | 测试条件 | 测试方法 | 测试结果 |
|---|
| 熔融温度 | | 内部方法 | 98.9to130 °C |
| TMA4 | High:635.0µm | 内部方法 | 145 °C |
| TMA4 | Low:635.0µm | 内部方法 | 110 °C |
| 机械性能 | 测试条件 | 测试方法 | 测试结果 |
|---|
| Abrasion2 | -- | DIN53516 | 43 mm³ |
| Abrasion2 | -- | ASTMD395 | 43 mm³ |
免责声明：此数据表中的信息由 Plas.Com 从该材料的生产商或第三方处获得。Plas.Com 尽最大努力确保此数据的准确性。 但是 Plas.Com 对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。