PVOH MonoSol® AF L711 美国MonoSol
0
比对物性数据
| 物理性能 | 测试条件 | 测试方法 | 测试结果 |
|---|---|---|---|
| 含水量 | 23°C | 7.1 wt% | |
| 可溶性 | Disintegration:10°C,35.0µm | 12.0 sec | |
| Disintegration:24°C,35.0µm | 5.0 sec | ||
| Dissolution:10°C,35.0µm | 120.0 sec | ||
| Dissolution:24°C,35.0µm | 72.0 sec |
| 薄膜 | 测试条件 | 测试方法 | 测试结果 |
|---|---|---|---|
| 割线模量 | 10%,TD:36µm | ASTMD882 | 82.7 MPa |
| 100%,TD:36µm | ASTMD882 | 22.8 MPa | |
| 拉伸强度 | MD:断裂,36µm | ASTM D882 | 45.5 MPa |
| TD:断裂,36µm | ASTM D882 | 43.4 MPa | |
| MD:36µm | ISO 527-3 | 45.5 MPa | |
| TD:36µm | ISO 527-3 | 43.4 MPa | |
| 伸长率 | MD:断裂,36µm | ASTMD882 | 180 % |
| 埃尔曼多夫撕裂强度 | TD:36µm | ISO 6383-2 | 0.040 N |
| 用量 | 35.0µm | ASTM D4321 | 22.9 m²/kg |
| 薄膜厚度 | 20µmto60µm | ||
| 割线模量 | 10%,MD:36µm | ASTMD882 | 89.6 MPa |
| 薄膜厚度 | 35 µm | ||
| 伸长率 | TD:断裂,36µm | ASTMD882 | 230 % |
| 落镖冲击 | 36µm | ASTMD1709 | 560 g |
| 埃尔曼多夫撕裂强度 | MD:36µm | ASTM D1922 | 390 g |
| TD:36µm | ASTM D1922 | 390 g | |
| MD:36µm | ISO 6383-2 | 0.040 N | |
| 割线模量 | 100%,MD:36µm | ASTMD882 | 33.8 MPa |
免责声明：此数据表中的信息由 Plas.Com 从该材料的生产商或第三方处获得。Plas.Com 尽最大努力确保此数据的准确性。 但是 Plas.Com 对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。