Ethylene Copolymer Exac ECTFE
0
- 特性:机械性能
- 典型应用:阀门阀门部件密封件泵件轴承汽车领域的应用航空航天应用衬套医疗器械电气元件绝缘材料连接器
比对物性数据
| 测试条件 | 测试方法 | 测试结果 | |
|---|---|---|---|
| 弯曲模量 | 23°C | ASTM D790 | 1690 MPa |
| 线性热膨胀系数 | MD | ASTM D696 | 1E-04 cm/cm/°C |
| 体积电阻率 | 23°C | ASTM D257 | 5.4E+16到5.5E+16 ohms·cm |
| 介电强度 | 23°C | ASTM D149 | 14to19 kV/mm |
| 邵氏硬度 | 23°C | ASTM D2240 | 75 |
| 拉伸模量 | 23°C | ASTM D638 | 1650to1660 MPa |
| 拉伸强度 | 屈服,23°C | ASTM D638 | 29.6to30.1 MPa |
| 断裂,23°C | ASTM D638 | 46.5to54.0 MPa | |
| 伸长率 | 屈服,23°C | ASTM D638 | 5.0to9.9 % |
| 断裂,23°C | ASTM D638 | 240to250 % | |
| 热变形温度 | 0.45MPa,未退火，HDT | ASTM D648 | 90.0to90.6 °C |
| 1.8MPa,未退火，HDT | ASTM D648 | 64.9to65.2 °C | |
| 脆化温度 | ASTM D746 | -76.1--73.7 °C | |
| 熔融温度 | 225to242 °C | ||
| 结晶峰温度 | DSC | ASTM D3418 | 222to223 °C |
| 密度 | ASTM D792 | 1.68 g/cm³ | |
| 熔体质量流动速率 | 275°C/2.16kg | ASTM D1238 | 1.0to25 g/10min |
| 洛氏硬度 | 23°C | ASTM D785 | 90 |
| 弯曲强度 | 23°C | ASTM D790 | 47.0 MPa |
| 摩擦系数 | ASTM D1894 | 0.20 | |
| 介电常数 | 23°C | ASTM D150 | 2.57 |
| 极限氧指数 | ASTM D2863 | 52 % |