PVOH MonoSol® AF L711 Blue 40µ 美国MonoSol
0
比对物性数据
| 物理性能 | 测试条件 | 测试方法 | 测试结果 |
|---|---|---|---|
| 可溶性 | Dissolution:10°C,40.0µm | 74.0 sec | |
| Dissolution:24°C,40.0µm | 58.0 sec | ||
| 含水量 | 23°C | 6.7 wt% | |
| 可溶性 | Disintegration:10°C,40.0µm | 16.0 sec | |
| Disintegration:24°C,40.0µm | 10.0 sec |
| 薄膜 | 测试条件 | 测试方法 | 测试结果 |
|---|---|---|---|
| 薄膜厚度 | 40 µm | ||
| 20µmto60µm | |||
| 割线模量 | 10%,MD:40µm | ASTMD882 | 101 MPa |
| 100%,MD:40µm | ASTMD882 | 37.2 MPa | |
| 10%,TD:40µm | ASTMD882 | 76.5 MPa | |
| 拉伸强度 | MD:40µm | ISO 527-3 | 51.0 MPa |
| TD:40µm | ISO 527-3 | 40.7 MPa | |
| 伸长率 | MD:断裂,40µm | ASTMD882 | 190 % |
| TD:断裂,40µm | ASTMD882 | 330 % | |
| 埃尔曼多夫撕裂强度 | MD:40µm | ASTM D1922 | 1400 g |
| TD:40µm | ASTM D1922 | 1200 g | |
| MD:40µm | ISO 6383-2 | 0.14 N | |
| TD:40µm | ISO 6383-2 | 0.12 N | |
| 用量 | 40.0µm | ASTM D4321 | 20.1 m²/kg |
| 割线模量 | 100%,TD:40µm | ASTMD882 | 16.5 MPa |
| 拉伸强度 | MD:断裂,40µm | ASTM D882 | 51.0 MPa |
| TD:断裂,40µm | ASTM D882 | 40.7 MPa |