MMW-HDPE TOTAL Polyethylene HDPE 6410 TOTAL
0
比对物性数据
| 物理性能 | 测试条件 | 测试方法 | 测试结果 |
|---|---|---|---|
| 密度 | ASTMD792 | 0.961 g/cm³ | |
| 熔体质量流动速率 | 190°C/2.16kg | ASTMD1238 | 1.2 g/10min |
| 190°C/21.6kg | ASTMD1238 | 33 g/10min |
| 薄膜 | 测试条件 | 测试方法 | 测试结果 |
|---|---|---|---|
| 拉伸应变-MD | Break,25µm,BlownFilm | ASTMD882A | 700 % |
| 拉伸应变 | Break,25µm,BlownFilm | ASTMD882A | 700 % |
| ElmendorfTearStrength-MD | 25µm,BlownFilm | ASTMD1922 | 24 g |
| ElmendorfTearStrength-TD | 25µm,BlownFilm | ASTMD1922 | 390 g |
| WaterVaporTransmissionRate | 38°C,25µm,BlownFilm | ASTMF1249 | 6.2 g/m²/24hr |
| 割线模量 | 1%正割,TD:25µm,吹塑薄膜 | ASTMD882A | 883 MPa |
| 2%Secant,TD:25µm,BlownFilm | ASTMD882A | 703 MPa | |
| 拉伸强度 | Yield,25µm,BlownFilm | ASTMD882A | 26.2 MPa |
| Yield,25µm,BlownFilm | ASTMD882A | 27.6 MPa | |
| Break,25µm,BlownFilm | ASTMD882A | 51.7 MPa | |
| Break,25µm,BlownFilm | ASTMD882A | 23.4 MPa | |
| 薄膜厚度-经测试 | 25 µm | ||
| 割线模量 | 1%正割,MD:25µm,吹塑薄膜 | ASTMD882A | 862 MPa |
| 2%Secant,MD:25µm,BlownFilm | ASTMD882A | 689 MPa |
| 光学性能 | 测试条件 | 测试方法 | 测试结果 |
|---|---|---|---|
| GardnerGloss | 25.4µm,BlownFilm | ASTMD523 | 50 |
| 雾度 | 25.4µm,吹塑薄膜 | ASTMD1003 | 15 % |
| 热性能 | 测试条件 | 测试方法 | 测试结果 |
|---|---|---|---|
| 熔融峰值温度 | ASTMD3417 | 134 °C |
免责声明：此数据表中的信息由 Plas.Com 从该材料的生产商或第三方处获得。Plas.Com 尽最大努力确保此数据的准确性。 但是 Plas.Com 对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。