原料比对
产品信息
品名
品牌名
典型应用
特性
认证
ABS MG47F-NA1000 SABIC INNOVATIVE MEXICO
CYCOLAC™
--
High impact resistance
UL
FDA
RoHS
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
物性数据
| Thermal Properties | 测试条件 | 测试方法 | SABIC INNOVATIVE MEXICO/MG47F-NA1000 |
|---|---|---|---|
| RTI | UL 746 | 60.0 °C | |
| Deflection Temperature Under Load? | 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 7 | ISO 75-2/Af | 81.0 °C |
| Linear thermal expansion coefficient | 横向 : -40 到 40°C | ASTM E831 | 8.8E-5 cm/cm/°C |
| Vicat Softening Temperature | -- | ISO 306/B50 | 98.0 °C |
| -- | ISO 306/B120 | 100 °C | |
| RTI Imp | UL 746 | 60.0 °C | |
| Vicat Softening Temperature | -- | ASTM D15258 | 99.0 °C |
| RTI Elec | UL 746 | 60.0 °C | |
| Deflection Temperature Under Load? | 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 80.0 °C |
| Linear thermal expansion coefficient | 流动 : -40 到 40°C | ASTM E831 | 8.8E-5 cm/cm/°C |
| Deflection Temperature Under Load? | 0.45 MPa, 未退火, 3.20 mm | ASTM D648 | 94.0 °C |
| Hardness | 测试条件 | 测试方法 | SABIC INNOVATIVE MEXICO/MG47F-NA1000 |
|---|---|---|---|
| Rockwell Hardness | R 级 | ASTM D785 | 112 |
| Fill Analysis | 测试条件 | 测试方法 | SABIC INNOVATIVE MEXICO/MG47F-NA1000 |
|---|---|---|---|
| Melt Viscosity | 240°C, 1000 sec^-1 | ASTM D3835 | 225 Pa·s |
| Injection | 测试条件 | 测试方法 | SABIC INNOVATIVE MEXICO/MG47F-NA1000 |
|---|---|---|---|
| Middle Temperature | 205 到 225 °C | ||
| Drying Time | 2.0 到 4.0 hr | ||
| Suggested Shot Size | 50 到 70 % | ||
| Drying Temperature | 80 到 95 °C | ||
| Mold Temperature | 50 到 70 °C | ||
| Vent Depth | 0.038 到 0.051 mm | ||
| Suggested Max Moisture | 0.10 % | ||
| Processing (Melt) Temp | 220 到 260 °C | ||
| Rear Temperature | 190 到 210 °C | ||
| Nozzle Temperature | 220 到 260 °C | ||
| Front Temperature | 215 到 240 °C | ||
| Back Pressure | 0.300 到 0.700 Mpa | ||
| Screw Speed | 30 到 60 rpm |
| Physical | 测试条件 | 测试方法 | SABIC INNOVATIVE MEXICO/MG47F-NA1000 |
|---|---|---|---|
| Melt Mass-Flow Rate | 220°C/10.0 kg | ISO 1133 | 18 g/10 min |
| 230°C/3.8 kg | ASTM D1238 | 5.6 g/10 min | |
| Modeling Shrinkage - Flow | 3.20 mm | 内部方法 | 0.50 到 0.80 % |
| Mechanical Properties | 测试条件 | 测试方法 | SABIC INNOVATIVE MEXICO/MG47F-NA1000 |
|---|---|---|---|
| Tensile Strength | 断裂 | ISO 527-2/50 | 35.0 Mpa |
| Tensile Modulus | -- | ISO 527-2/1 | 2370 Mpa |
| Tensile Elongation | 断裂 2 | ASTM D638 | 24 % |
| Tensile Strength | 屈服 2 | ASTM D638 | 44.0 Mpa |
| Tensile Elongation | 屈服 | ISO 527-2/50 | 2.6 % |
| Flexural Modulus | 50.0 mm 跨距 3 | ASTM D790 | 2300 Mpa |
| Tensile Modulus | -- 1 | ASTM D638 | 2270 Mpa |
| Tensile Strength | 屈服 | ISO 527-2/50 | 47.0 Mpa |
| Flexural Modulus | -- 4 | ISO 178 | 2200 Mpa |
| Flexural Stress | 屈服, 50.0 mm 跨距 3 | ASTM D790 | 70.0 Mpa |
| -- 4, 5 | ISO 178 | 70.0 Mpa | |
| Tensile Elongation | 屈服 2 | ASTM D638 | 2.0 % |
| 断裂 | ISO 527-2/50 | 25 % | |
| Tensile Strength | 断裂 2 | ASTM D638 | 33.0 Mpa |
| Impact Properties | 测试条件 | 测试方法 | SABIC INNOVATIVE MEXICO/MG47F-NA1000 |
|---|---|---|---|
| Instrumented Dart Impact | 23°C, Total Energy | ASTM D3763 | 30.0 J |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 9.0 kJ/m² |
| 23°C | ISO 179/1eA | 26 kJ/m² |
| Flammability | 测试条件 | 测试方法 | SABIC INNOVATIVE MEXICO/MG47F-NA1000 |
|---|---|---|---|
| UL flame retardant rating | 1.5 mm | UL 94 | HB |
| Electrical Properties | 测试条件 | 测试方法 | SABIC INNOVATIVE MEXICO/MG47F-NA1000 |
|---|---|---|---|
| Hot-wire Ignition | UL 746 | PLC 3 | |
| Arc Resistance | ASTM D495 | PLC 6 | |
| Comparative Tracking Index | UL 746 | PLC 0 | |
| High Amp Arc Ignition | UL 746 | PLC 0 | |
| High Voltage Arc Tracking Rate | UL 746 | PLC 3 |