原料比对
产品信息
品名
品牌名
典型应用
特性
认证
TPE 5526 DUPONT USA
Hytrel®
Automotive sector、Electrical appliances、Fitness equipment、Electronic field、Electrical field
Weather resistance、UV resistance、High mobility、Thermal stability
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
物性数据
| Thermal Properties | 测试条件 | 测试方法 | DUPONT USA/5526 |
|---|---|---|---|
| Glass Transition Temperature | ISO11357-2 | -20.0 °C | |
| Vicat Softening Temperature | -- | ISO306/B50 | 75.0 °C |
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO75-2/B | 65.0 °C |
| Brittleness Temperature | ISO974 | -98.0 °C | |
| Linear thermal expansion coefficient | TD：-- | ISO11359-2 | 2E-04 cm/cm/°C |
| Heat Deflection Temperature | 1.8MPa,未退火 | ISO75-2/A | 45.0 °C |
| Vicat Softening Temperature | -- | ISO306/A50 | 180 °C |
| Melting Temperature | ISO11357-3 | 203 °C | |
| Linear thermal expansion coefficient | MD：-40to23°C | ISO11359-2 | 1.8E-04 cm/cm/°C |
| MD：-- | ISO11359-2 | 2E-04 cm/cm/°C | |
| TD：EffectiveThermalDiffusivity | ISO11359-2 | 9E-08 m²/s | |
| TD：-40to23°C | ISO11359-2 | 1.7E-04 cm/cm/°C |
| Hardness | 测试条件 | 测试方法 | DUPONT USA/5526 |
|---|---|---|---|
| Shore Hardness | 邵氏D | ISO868 | 55 |
| 邵氏D,15秒 | ISO868 | 51 |
| Elastomers Properties | 测试条件 | 测试方法 | DUPONT USA/5526 |
|---|---|---|---|
| Tearing Strength | 横向流量 | ISO34-1 | 130 kN/m |
| 流量 | ISO34-1 | 130 kN/m |
| Additional | 测试条件 | 测试方法 | DUPONT USA/5526 |
|---|---|---|---|
| Odor | VDA270 | 5.00 |
| Physical | 测试条件 | 测试方法 | DUPONT USA/5526 |
|---|---|---|---|
| Density / Specific Gravity | ISO1183 | 1.19 g/cm³ | |
| SpecificHeatCapacityofMelt | 2110 J/kg/°C | ||
| Moisture Absorption | 平衡,23°C,2.00mm,50%RH | ISO62 | 0.20 % |
| 饱和,23°C,2.00mm | ISO62 | 0.60 % | |
| ThermalConductivityofMelt | 0.19 W/m/K | ||
| MediumDensity | 1.04 g/cm³ | ||
| Melt Mass-Flow Rate | ISO1133 | 18 g/10min | |
| Melt Volume flow Rate | 220°C/2.16kg | ISO1133 | 17.5 cm3/10min |
| Modeling Shrinkage | TD | ISO294-4 | 1.4 % |
| MD | ISO294-4 | 1.4 % | |
| Moisture Absorption | 23°C,24hr | ISO62 | 0.60 % |
| Mechanical Properties | 测试条件 | 测试方法 | DUPONT USA/5526 |
|---|---|---|---|
| Tensile Stress | 10%应变 | ISO527-2 | 11.0 Mpa |
| Tensile Strain | 屈服 | ISO527-2 | 35 % |
| Tensile Stress | 5.0%应变 | ISO527-2 | 6.90 Mpa |
| 屈服 | ISO527-2 | 15.0 Mpa | |
| Flexural Modulus | ISO178 | 200 Mpa | |
| Tensile Creep Modulus | 1000hr | ISO899-1 | 130 Mpa |
| Abrasion Resistance | ISO4649 | 120 mm³ | |
| Tensile Strain | 断裂 | ISO527-2 | >300 % |
| Nominal Tensile Strain at Break | ISO527-2 | 780 % | |
| Tensile Stress | 断裂 | ISO527-2 | 40.0 Mpa |
| Tensile Modulus | ISO527-2 | 190 Mpa | |
| Tensile Creep Modulus | 1hr | ISO899-1 | 170 Mpa |
| Tensile Stress | 50%应变 | ISO527-2 | 14.0 Mpa |
| Impact Properties | 测试条件 | 测试方法 | DUPONT USA/5526 |
|---|---|---|---|
| Tensile Impact Strength | 23°C | ISO8256/1 | 270 kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | NoBreak |
| -30°C,局部断裂 | ISO179/1eA | 150 kJ/m² | |
| -40°C | ISO179/1eA | 30 kJ/m² | |
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | NoBreak |
| 23°C | ISO179/1eU | NoBreak |
| Flammability | 测试条件 | 测试方法 | DUPONT USA/5526 |
|---|---|---|---|
| Burning Rate | 1.00mm | ISO3795 | 28 mm/min |
| Flame Rating | 3.0mm | IEC60695-11-10,-20 | HB |
| 1.5mm | IEC60695-11-10,-20 | HB | |
| Fogging-G-value | condensate | ISO6452 | 1E-04 g |
| Oxygen Index | ISO4589-2 | 21 % | |
| Flame Rating | 3.0mm | UL94 | HB |
| 1.5mm | UL94 | HB | |
| FMVSS Flammability | FMVSS302 | SE/B |
| Electrical Properties | 测试条件 | 测试方法 | DUPONT USA/5526 |
|---|---|---|---|
| Relative Permittivity | 100Hz | IEC60250 | 4.90 |
| Dielectric Strength | IEC60243-1 | 20 KV/mm | |
| Dissipation Factor? | 1MHz | IEC60250 | 0.038 |
| Volume Resistivity | IEC60093 | 4E+13 ohms·cm | |
| Comparative Tracking Index | IEC60112 | 600 V | |
| Surface Resistivity | IEC60093 | >1.0E+15 ohms | |
| Relative Permittivity | 1MHz | IEC60250 | 4.60 |
| Dissipation Factor? | 100Hz | IEC60250 | 9E-03 |