TPE 8211-55B100 EXXONMOBIL USA
Santoprene™
Washer、diaphragm、Kitchen utensils、Household appliances、Home appliance components、Movable hinge、Adhesive resin
wear resistant、Aging resistance、UV resistance、Weather resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
物性数据
| Elastomers Properties | 测试条件 | 测试方法 | EXXONMOBIL USA/8211-55B100 |
|---|---|---|---|
| Compression Set | 125°C,70hr | ASTMD395B | 55 % |
| Tensile Elongation(Across Flow) | 断裂,23°C | ASTMD412 | 600 % |
| Compression Set | 125°C,70hr | ISO815 | 55 % |
| Tensile Elongation(Across Flow) | 断裂,23°C | ISO37 | 600 % |
| Hardness | 测试条件 | 测试方法 | EXXONMOBIL USA/8211-55B100 |
|---|---|---|---|
| Shore Hardness | 邵氏A,15秒,23°C | ISO868 | 53 |
| Aging Properties | 测试条件 | 测试方法 | EXXONMOBIL USA/8211-55B100 |
|---|---|---|---|
| Change in Tensile Strength in Air | 100°C,168hr | ASTMD573 | -28 % |
| Change in Tensile Strength | 23°C,168hr,inSodiumHydroxide,50% | ISO1817 | 1.0 % |
| Tensile Stress(Break) | 23°C,168hr,inIRM903Oil | ISO1817 | -68 % |
| Change in Tensile Strength in Air | 100°C,168hr | ISO188 | -28 % |
| ChangeinShoreHardness | ShoreA,23°C,168hr,inIRM903Oil | ISO1817 | -33 |
| Tensile Stress(Break) | 23°C,168hr,inHydrochloricAcid,10% | ISO1817 | -9.0 % |
| Change in Durometer Hardness | ShoreA,23°C,168hr,inSodiumHydroxide,50% | ASTMD471 | 4.0 |
| Tensile Stress(Break) | 23°C,168hr,在水中 | ISO1817 | -12 % |
| Change in Tensile Strength | 23°C,168hr,inSodiumHydroxide,50% | ASTMD471 | 1.0 % |
| Change in Ultimate Elongation | 23°C,168hr,inHydrochloricAcid,10% | ASTMD471 | -9.0 % |
| Change in Ultimate Elongation in Air | 100°C,168hr | ASTMD573 | -14 % |
| Change in Ultimate Elongation | 23°C,168hr,inIRM903Oil | ASTMD471 | -68 % |
| Change in Tensile Strength | 23°C,168hr,inIRM903Oil | ASTMD471 | -85 % |
| 23°C,168hr,在水中 | ASTMD471 | 2.0 % | |
| 23°C,168hr,inHydrochloricAcid,10% | ASTMD471 | -1.0 % | |
| Change in Durometer Hardness | ShoreA,23°C,168hr,inIRM903Oil | ASTMD471 | -33 |
| Change in Tensile Strength | 23°C,168hr,inEthanol,95% | ISO1817 | -17 % |
| Change in Tensile Strain at Break in Air? | 100°C,168hr | ISO188 | -14 % |
| Change in Tensile Strength | 23°C,168hr,inHydrochloricAcid,10% | ISO1817 | -1.0 % |
| Change in Ultimate Elongation | 23°C,168hr,在水中 | ASTMD471 | -12 % |
| Change in Durometer Hardness | ShoreA,23°C,168hr,inHydrochloricAcid,10% | ASTMD471 | 4.0 |
| Change in Tensile Strain at Break in Air? | 125°C,168hr | ISO188 | -70 % |
| Change in Shore Hardness in Air | ShoreA,100°C,168hr | ISO188 | -4.0 |
| ChangeinShoreHardness | ShoreA,23°C,168hr,inHydrochloricAcid,10% | ISO1817 | 4.0 |
| Tensile Stress(Break) | 23°C,168hr,inEthanol,95% | ISO1817 | -3.0 % |
| ChangeinShoreHardness | ShoreA,23°C,168hr,inEthanol,95% | ISO1817 | 2.0 |
| Change in Durometer Hardness in Air | 邵氏A,125°C,168hr | ASTMD573 | 8.0 |
| Change in Ultimate Elongation | 23°C,168hr,inSodiumHydroxide,50% | ASTMD471 | -7.0 % |
| Change in Ultimate Elongation in Air | 125°C,168hr | ASTMD573 | -70 % |
| Change in Tensile Strength in Air | 125°C,168hr | ASTMD573 | -61 % |
| 125°C,168hr | ISO188 | -61 % | |
| Change in Ultimate Elongation | 23°C,168hr,inEthanol,95% | ASTMD471 | -3.0 % |
| Change in Durometer Hardness | ShoreA,23°C,168hr,inWater | ASTMD471 | 5.0 |
| ChangeinShoreHardness | ShoreA,23°C,168hr,inSodiumHydroxide,50% | ISO1817 | 4.0 |
| Change in Durometer Hardness | ShoreA,23°C,168hr,inEthanol,95% | ASTMD471 | 2.0 |
| Change in Tensile Strength | 23°C,168hr,在水中 | ISO1817 | 2.0 % |
| Tensile Stress(Break) | 23°C,168hr,inSodiumHydroxide,50% | ISO1817 | -7.0 % |
| Change in Shore Hardness in Air | 邵氏A,125°C,168hr | ISO188 | 8.0 |
| Change in Tensile Strength | 23°C,168hr,inIRM903Oil | ISO1817 | -85 % |
| 23°C,168hr,inEthanol,95% | ASTMD471 | -17 % | |
| ChangeinShoreHardness | ShoreA,23°C,168hr,inWater | ISO1817 | 5.0 |
| Change in Durometer Hardness in Air | ShoreA,100°C,168hr | ASTMD573 | -4.0 |
| Flammability | 测试条件 | 测试方法 | EXXONMOBIL USA/8211-55B100 |
|---|---|---|---|
| Flame Rating | 2.9mm | UL94 | HB |
| 1.1mm | UL94 | HB |