PC/PET X8300 SABIC INNOVATIVE US
XYLEX™
Electronic field、Electrical field
UV resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
物性数据
| Thermal Properties | 测试条件 | 测试方法 | SABIC INNOVATIVE US/X8300 |
|---|---|---|---|
| Vicat Softening Temperature | ISO306/B120 | 96.0 °C | |
| Thermal Conductivity | ISO8302 | 0.23 W/m/K | |
| Heat Deflection Temperature | 1.8MPa,未退火,100mm跨距9 | ISO75-2/Ae | 80.0 °C |
| Vicat Softening Temperature | ASTMD152511 | 91.0 °C | |
| Heat Deflection Temperature | 1.8MPa,未退火,3.20mm | ASTMD648 | 75.0 °C |
| Linear thermal expansion coefficient | MD：-40到40°C | ASTME831 | 1.1E-04 cm/cm/°C |
| MD：23to60°C | ISO11359-2 | 9E-05 cm/cm/°C | |
| TD：-40to40°C | ISO11359-2 | 1.1E-04 cm/cm/°C | |
| MD：-40to40°C | ISO11359-2 | 1.1E-04 cm/cm/°C | |
| Heat Deflection Temperature | 0.45MPa,未退火,3.20mm | ASTMD648 | 79.0 °C |
| Linear thermal expansion coefficient | TD：-40到40°C | ASTME831 | 1.1E-04 cm/cm/°C |
| TD：23to60°C | ISO11359-2 | 9E-05 cm/cm/°C | |
| Ball PressureTest | 85°C | IEC60695-10-2 | Pass |
| Heat Deflection Temperature | 1.8MPa,未退火,64.0mm跨距10 | ISO75-2/Af | 78.0 °C |
| Hardness | 测试条件 | 测试方法 | SABIC INNOVATIVE US/X8300 |
|---|---|---|---|
| Shore Hardness | 邵氏D,10秒 | ASTMD2240 | 74 |
| Physical | 测试条件 | 测试方法 | SABIC INNOVATIVE US/X8300 |
|---|---|---|---|
| Moisture Absorption | 平衡,23°C,50%RH | ISO62 | 0.20 % |
| Density / Specific Gravity | ISO1183 | 1.17 g/cm³ | |
| ASTMD792 | 1.20 g/cm³ | ||
| Melt Mass-Flow Rate | 265°C/2.16kg | ASTMD1238 | 15 g/10min |
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.50to0.80 % |
| TD：3.20mm | 内部方法 | 0.40to0.60 % | |
| Moisture Absorption | 饱和,23°C | ISO62 | 0.050 % |
| Melt Volume flow Rate | 265°C/2.16kg | ISO1133 | 15.0 cm3/10min |
| Mechanical Properties | 测试条件 | 测试方法 | SABIC INNOVATIVE US/X8300 |
|---|---|---|---|
| Flexural Modulus | 50.0mm跨距 | ASTMD790 | 1680 Mpa |
| Tensile Stress | 断裂 | ISO527-2/50 | 54.0 Mpa |
| Tensile Elongation | 断裂 | ASTMD638 | 150 % |
| Tensile Strain | 断裂 | ISO527-2/50 | >200 % |
| Tensile Modulus | ISO527-2/1 | 1600 Mpa | |
| Tensile Strength | 屈服 | ASTMD638 | 47.0 Mpa |
| Flexural Modulus | ISO178 | 1700 Mpa | |
| Flexural Strength | 屈服,50.0mm跨距 | ASTMD790 | 71.0 Mpa |
| Tensile Elongation | 屈服 | ASTMD638 | 5.0 % |
| Tensile Stress | 屈服 | ISO527-2/50 | 55.0 Mpa |
| Tensile Strain | 屈服 | ISO527-2/50 | >5.0 % |
| Flexural Strength | ISO178 | 78.0 Mpa | |
| Tensile Modulus | ASTMD638 | 1520 Mpa | |
| Tensile Strength | 断裂 | ASTMD638 | 46.0 Mpa |
| Optical | 测试条件 | 测试方法 | SABIC INNOVATIVE US/X8300 |
|---|---|---|---|
| Transmittance | 2540µm | ASTMD1003 | 88.0 % |
| Index of Refraction | ISO489 | 1.539 | |
| Haze | 2540µm | ASTMD1003 | 1.0 % |
| Impact Properties | 测试条件 | 测试方法 | SABIC INNOVATIVE US/X8300 |
|---|---|---|---|
| Notched Izod Impact Strength | -30°C | ISO180/1A | 7.0 kJ/m² |
| -10°C | ISO180/1A | 5.0 kJ/m² | |
| 23°C | ASTMD256 | 1100 J/m | |
| -30°C | ASTMD256 | 73 J/m | |
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 95.0 J |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 10 kJ/m² |
| Notched Izod Impact Strength | 23°C | ISO180/1A | 8.0 kJ/m² |
| Flammability | 测试条件 | 测试方法 | SABIC INNOVATIVE US/X8300 |
|---|---|---|---|
| Flame Rating | 3.0mm | UL94 | V-2 |
| Glow Wire Flammability Index | 1.0mm | IEC60695-2-12 | 750 °C |
| Electrical Properties | 测试条件 | 测试方法 | SABIC INNOVATIVE US/X8300 |
|---|---|---|---|
| Surface Resistivity | ASTMD257 | >1.0E+15 ohms | |
| Volume Resistivity | ASTMD257 | >1.0E+15 ohms·cm | |
| Comparative Tracking Index | CTI | UL746 | PLC 0 |