原料比对
产品信息
品名
品牌名
典型应用
特性
认证
EAA 1430 STYRON US
PRIMACOR™
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
物性数据
| Thermal Properties | 测试条件 | 测试方法 | STYRON US/1430 |
|---|---|---|---|
| Vicat Softening Temperature | ISO 306 | 76.1 ℃ | |
| Melting temperature (DSC) | 内部方法 | 96.1 °C | |
| Melting temperature | ℃ | Internal Method 96.1 | |
| Vicat Softening Temperature | ASTM D-1525 | 76.1 ℃ | |
| ASTMD1525,ISO306 | 76.1 °C |
| Films Properties | 测试条件 | 测试方法 | STYRON US/1430 |
|---|---|---|---|
| Tensile Elongation | MD:断裂,51µm | ASTMD882,ISO527-3 | 420 % |
| Tensile Strength | MD:屈服,51µm | ASTMD882 | 10.4 Mpa |
| Elmendorf Tear Strength | MD:51µm | ISO6383-2 | 2100 N |
| Tensile Strength | TD:屈服,51µm | ASTMD882 | 10.2 Mpa |
| TD:断裂,51µm | ASTMD882,ISO527-3 | 31.0 Mpa | |
| Elmendorf Tear Strength | TD:51µm | ASTMD1922 | 730 g |
| MD:51µm | ASTMD1922 | 470 g | |
| Tensile Strength | TD:屈服,51µm | ISO527-3 | 10.2 Mpa |
| MD:屈服,51µm | ISO527-3 | 10.4 Mpa | |
| Elmendorf Tear Strength | TD:51µm | ISO6383-2 | 3300 N |
| Tensile Strength | MD:断裂,51µm | ASTMD882,ISO527-3 | 30.6 Mpa |
| Tensile Elongation | TD:断裂,51µm | ASTMD882,ISO527-3 | 470 % |
| Mechanical Properties | 测试条件 | 测试方法 | STYRON US/1430 |
|---|---|---|---|
| Tensile Strength | 屈服,模压成型4 | ASTMD638 | 7.67 Mpa |
| Tensile Elongation (Break MD) | 50.8um | ISO 527-3 | 420 % |
| Tensile Strength (Yield TD) | 50.8um | ASTM D-882 | 10.2 MPa |
| Elmendorf Tear Strength (MD) | 50.8um | ISO 6383-2 | 2100 N |
| Tensile Strength(Break) | Compression Molded | ISO 527-2/508 | 19.5 MPa |
| Tensile Elongation | 断裂,模压成型 | ISO527-2/508 | 580 % |
| Elmendorf Tear Strength (TD) | 50.8um | ASTM D-1922 | 730 g |
| Tensile Strength (Break TD) | 50.8um | ISO 527-3 | 30.6 MPa |
| Tensile Elongation?(Break) | Compression Molded | ASTM D-638 | 580 % |
| Tensile Strength (Yield MD) | 50.8um | ISO 527-3 | 10.4 MPa |
| Tensile Strength (Break TD) | 50.8um | ASTM D-882 | 30.6 MPa |
| Tensile Strength(Break) | Compression Molded | ASTM D-638 | 19.5 MPa |
| Tensile Elongation?(Break) | Compression Molded | ISO 527-2/508 | 580 % |
| Elmendorf Tear Strength (TD) | 50.8um | ISO 6383-2 | 3300 N |
| Tensile Strength (Yield TD) | 50.8um | ISO 527-3 | 10.2 MPa |
| Tensile Elongation (Break TD) | 50.8um | ASTM D-882 | 470 % |
| 50.8um | ISO 527-3 | 470 % | |
| Elmendorf Tear Strength (MD) | 50.8um | ASTM D-1922 | 470 g |
| Tensile Strength | 断裂,模压成型4 | ASTMD638 | 19.5 Mpa |
| Tensile Elongation (Break MD) | 50.8um | ASTM D-882 | 420 % |
| Tensile Strength(Yield) | Compression Molded | ISO 527-2/508 | 7.67 MPa |
| Tensile Strength (Yield MD) | 50.8um | ASTM D-882 | 10.4 MPa |
| Tensile Strength | 断裂,模压成型 | ISO527-2/508 | 19.5 Mpa |
| Tensile Elongation | 断裂,模压成型4 | ASTMD638 | 580 % |
| Tensile Strength | 屈服,模压成型 | ISO527-2/508 | 7.67 Mpa |
| Tensile Strength(Yield) | Compression Molded | ASTM D-638 | 7.67 MPa |
| Physical | 测试条件 | 测试方法 | STYRON US/1430 |
|---|---|---|---|
| monomer Content | % | Internal Method 9.7 | |
| Melt Mass-Flow Rate | 190℃/2.16kg | ISO 1133 | 5 g/10min |
| Density / Specific Gravity | ASTMD792,ISO1183 | 0.930 g/cm³ | |
| Melt Mass-Flow Rate | 190℃/2.16kg | ASTM D-1238 | 5 g/10min |
| monomer Content | 内部方法 | 9.7 % | |
| Density / Specific Gravity | ASTM D-792 | 0.93 g/cm³ | |
| ISO 1183 | 0.93 g/cm³ | ||
| Melt Mass-Flow Rate | 190°C/2.16kg | ASTMD1238,ISO1133 | 5.0 g/10min |
| Optical | 测试条件 | 测试方法 | STYRON US/1430 |
|---|---|---|---|
| Haze | 50.8µm | ISO14782 | 4.0 % |
| 50.8um | ASTM D-1003 | 4 % | |
| Gloss | 45°，50.8um | ASTM D-2457 | 74 |
| Haze | 50.8µm | ASTMD1003 | 4.0 % |
| 50.8um | ISO 14782 | 4 % | |
| Gloss | 45°,50.8µm | ASTMD2457 | 74 |