原料比对
产品信息
品名
品牌名
典型应用
特性
认证
PC/PET X7300CL NA9A002 SABIC INNOVATIVE US
XYLEX™
Automotive sector
UV resistance、High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
物性数据
| Thermal Properties | 测试条件 | 测试方法 | SABIC INNOVATIVE US/X7300CL NA9A002 |
|---|---|---|---|
| Heat Deflection Temperature | 1.8MPa,Unannealed,100mmSpan | ISO75-2/Ae | 90.0 °C |
| Vicat Softening Temperature | ISO306/B120 | 106 °C | |
| Linear thermal expansion coefficient | MD：23到60°C | ISO11359-2 | 8.5E-05 cm/cm/°C |
| Heat Deflection Temperature | 0.45MPa,未退火,3.20mm | ASTMD648 | 102 °C |
| Linear thermal expansion coefficient | TD：-40到40°C | ASTME831 | 1.1E-04 cm/cm/°C |
| TD：23to60°C | ISO11359-2 | 8.5E-05 cm/cm/°C | |
| Heat Deflection Temperature | 1.8MPa,未退火,3.20mm | ASTMD648 | 88.0 °C |
| Vicat Softening Temperature | ASTMD15259 | 108 °C | |
| Linear thermal expansion coefficient | MD：-40到40°C | ASTME831 | 1.2E-04 cm/cm/°C |
| Physical | 测试条件 | 测试方法 | SABIC INNOVATIVE US/X7300CL NA9A002 |
|---|---|---|---|
| Melt Mass-Flow Rate | 265°C/2.16kg | ASTMD1238 | 21 g/10min |
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.40to0.80 % |
| TD：3.20mm | 内部方法 | 0.50to0.70 % | |
| Melt Volume flow Rate | 265°C/2.16kg | ISO1133 | 21.0 cm3/10min |
| Mechanical Properties | 测试条件 | 测试方法 | SABIC INNOVATIVE US/X7300CL NA9A002 |
|---|---|---|---|
| Flexural Modulus | 50.0mm跨距 | ASTMD790 | 1940 Mpa |
| Tensile Stress | 断裂 | ISO527-2/50 | 55.0 Mpa |
| Tensile Elongation | 断裂 | ASTMD638 | 150 % |
| Tensile Strain | 断裂 | ISO527-2/50 | >150 % |
| Tensile Modulus | ISO527-2/1 | 1900 Mpa | |
| Tensile Strength | 屈服 | ASTMD638 | 49.0 Mpa |
| Flexural Modulus | ISO178 | 2000 Mpa | |
| Flexural Strength | 屈服,50.0mm跨距 | ASTMD790 | 83.0 Mpa |
| Tensile Elongation | 屈服 | ASTMD638 | 5.0 % |
| Tensile Stress | 屈服 | ISO527-2/50 | 55.0 Mpa |
| Tensile Strain | 屈服 | ISO527-2/50 | 5.0 % |
| Flexural Strength | ISO178 | 71.0 Mpa | |
| Tensile Modulus | ASTMD638 | 1840 Mpa | |
| Tensile Strength | 断裂 | ASTMD638 | 52.0 Mpa |
| Optical | 测试条件 | 测试方法 | SABIC INNOVATIVE US/X7300CL NA9A002 |
|---|---|---|---|
| Transmittance | 2540µm | ASTMD1003 | 88.0 % |
| Haze | 2540µm | ASTMD1003 | 2.0 % |
| Impact Properties | 测试条件 | 测试方法 | SABIC INNOVATIVE US/X7300CL NA9A002 |
|---|---|---|---|
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 95.0 J |
| Notched Izod Impact Strength | 23°C | ISO180/1A | 9.0 kJ/m² |