原料比对
产品信息
品名
品牌名
典型应用
特性
认证
PA6 PX09322 WH SABIC INNOVATIVE US
LNP™ KONDUIT™
Automotive components、Electronic and electrical
wear resistant、high strength、Filler: Mineral filler
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
物性数据
| Thermal Properties | 测试条件 | 测试方法 | SABIC INNOVATIVE US/PX09322 WH |
|---|---|---|---|
| Thermal Conductivity | --5 | ASTM D790/ISO 178 | 1.5 W/m/K |
| Heat Deflection Temperature | 1.8MPa,未退火,6.40mm | ASTMD648 | 182 °C |
| Thermal Conductivity | --7 | ISO22007-2 | 0.86 W/m/K |
| Linear thermal expansion coefficient | MD:-40到40°C | ASTME831 | 2.4E-05 cm/cm/°C |
| Thermal Conductivity | --6 | ASTM D790/ISO 178 | 6.0 W/m/K |
| Linear thermal expansion coefficient | TD:-40到40°C | ASTME831 | 3.7E-05 cm/cm/°C |
| Heat Deflection Temperature | 0.45MPa,未退火,6.40mm | ASTMD648 | 210 °C |
| Thermal Conductivity | --8 | ISO22007-2 | 2.7 W/m/K |
| Mechanical Properties | 测试条件 | 测试方法 | SABIC INNOVATIVE US/PX09322 WH |
|---|---|---|---|
| Flexural Modulus | 50.0mm跨距 | ASTMD790 | 11000 Mpa |
| Flexural Strength | 屈服,50.0mm跨距 | ASTMD790 | 80.0 Mpa |
| Tensile Elongation | 断裂 | ASTMD638 | 0.80 % |
| Tensile Modulus | ASTMD638 | 10400 Mpa | |
| Flexural Strength | 断裂,50.0mm跨距 | ASTMD790 | 81.0 Mpa |
| Tensile Strength | 断裂 | ASTMD638 | 51.0 Mpa |
| Physical | 测试条件 | 测试方法 | SABIC INNOVATIVE US/PX09322 WH |
|---|---|---|---|
| Modeling Shrinkage | MD | 内部方法 | 0.58 % |
| Moisture Absorption | 24hr,50%RH | ASTMD570 | 0.060 % |
| Modeling Shrinkage | TD | 内部方法 | 0.53 % |
| Impact Properties | 测试条件 | 测试方法 | SABIC INNOVATIVE US/PX09322 WH |
|---|---|---|---|
| Unnotched Izod Impact Strength | 23°C | ASTMD4812 | 130 J/m |
| Flammability | 测试条件 | 测试方法 | SABIC INNOVATIVE US/PX09322 WH |
|---|---|---|---|
| Flame Rating | 1.2mm | UL94 | V-0 |
| Glow Wire Flammability Index | 1.0mm | IEC60695-2-12 | 960 °C |
| Electrical Properties | 测试条件 | 测试方法 | SABIC INNOVATIVE US/PX09322 WH |
|---|---|---|---|
| Surface Resistivity | ASTMD257 | 8.1E+14 ohms | |
| Comparative Tracking Index | CTI | UL746 | PLC 0 |