原料比对
产品信息
品名
品牌名
典型应用
特性
认证
PBT V4860HR-GY6H015 SABIC INNOVATIVE SHANGHAI
VALOX™
Home appliance components、Automotive Applications
High rigidity、high strength
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
物性数据
| Thermal Properties | 测试条件 | 测试方法 | SABIC INNOVATIVE SHANGHAI/V4860HR-GY6H015 |
|---|---|---|---|
| Heat Deflection Temperature | 1.8MPa,未退火,6.40mm | ASTMD648 | 205 °C |
| 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 188 °C | |
| Vicat Softening Temperature | -- | ISO306/B50 | 176 °C |
| Linear thermal expansion coefficient | TD：-40to95°C | ASTME831 | 1.1E-04 cm/cm/°C |
| Ball PressureTest | 75°C | IEC60695-10-2 | Pass |
| Heat Deflection Temperature | 1.8MPa,未退火,3.20mm | ASTMD648 | 197 °C |
| Vicat Softening Temperature | -- | ISO306/B120 | 175 °C |
| Linear thermal expansion coefficient | MD：-40到95°C | ASTME831 | 2.4E-05 cm/cm/°C |
| MD：23到80°C | ISO11359-2 | 2.3E-05 cm/cm/°C | |
| Vicat Softening Temperature | ASTMD152512 | 176 °C | |
| Linear thermal expansion coefficient | TD：23to80°C | ISO11359-2 | 1.2E-04 cm/cm/°C |
| Heat Deflection Temperature | 0.45MPa,未退火,6.40mm | ASTMD648 | 221 °C |
| Mechanical Properties | 测试条件 | 测试方法 | SABIC INNOVATIVE SHANGHAI/V4860HR-GY6H015 |
|---|---|---|---|
| Flexural Modulus | 50.0mm跨距 | ASTMD790 | 6740 Mpa |
| Tensile Elongation | 断裂 | ASTMD638 | 2.3 % |
| Tensile Strain | 断裂 | ISO527-2/5 | 2.2 % |
| Tensile Modulus | ISO527-2/1 | 9450 Mpa | |
| Tensile Strength | 屈服 | ASTMD638 | 116 Mpa |
| Tensile Stress | 断裂 | ISO527-2/5 | 111 Mpa |
| Flexural Strength | 屈服,50.0mm跨距 | ASTMD790 | 174 Mpa |
| Flexural Modulus | ISO178 | 7880 Mpa | |
| Tensile Elongation | 屈服 | ASTMD638 | 2.3 % |
| Flexural Strain (Break) | ISO178 | 2.9 % | |
| Tensile Modulus | ASTMD638 | 9750 Mpa | |
| Flexural Strength | 断裂,50.0mm跨距 | ASTMD790 | 2.96 Mpa |
| Tensile Strain | 屈服 | ISO527-2/5 | 2.1 % |
| Flexural Stress | --6 | ISO178 | 182 Mpa |
| Tensile Strength | 断裂 | ASTMD638 | 115 Mpa |
| Flexural Stress | --7 | ISO178 | 183 Mpa |
| Tensile Stress | 屈服 | ISO527-2/5 | 112 Mpa |
| Physical | 测试条件 | 测试方法 | SABIC INNOVATIVE SHANGHAI/V4860HR-GY6H015 |
|---|---|---|---|
| Density / Specific Gravity | ISO1183 | 1.64 g/cm³ | |
| Moisture Absorption | 平衡,23°C,50%RH | ISO62 | 0.060 % |
| Melt Volume flow Rate | 250°C/5.0kg | ISO1133 | 12.4 cm3/10min |
| Density / Specific Gravity | ASTMD792 | 1.64 g/cm³ | |
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.50to0.70 % |
| Melt Mass-Flow Rate | 250°C/5.0kg | ASTMD1238 | 18 g/10min |
| Modeling Shrinkage | TD：3.20mm | 内部方法 | 0.50to1.0 % |
| Moisture Absorption | 饱和,23°C | ISO62 | 0.19 % |
| Impact Properties | 测试条件 | 测试方法 | SABIC INNOVATIVE SHANGHAI/V4860HR-GY6H015 |
|---|---|---|---|
| Notched Izod Impact Strength | -30°C | ISO180/1A | 8.5 kJ/m² |
| 23°C | ASTMD256 | 90 J/m | |
| -30°C | ASTMD256 | 74 J/m | |
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 13.4 J |
| 23°C | ISO179/1eA | 11 kJ/m² | |
| Notched Izod Impact Strength | 23°C | ISO180/1A | 10 kJ/m² |
| Flammability | 测试条件 | 测试方法 | SABIC INNOVATIVE SHANGHAI/V4860HR-GY6H015 |
|---|---|---|---|
| Flame Rating | 0.8mm,TestingbySABIC | UL94 | V-0 |