原料比对
产品信息
品名
品牌名
典型应用
特性
认证
PC/PBT X8300MR SABIC INNOVATIVE US
XENOY™
Automotive Applications
High mobility、High impact resistance、Dimensional stability
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
物性数据
| Thermal Properties | 测试条件 | 测试方法 | SABIC INNOVATIVE US/X8300MR |
|---|---|---|---|
| Thermal Conductivity | ISO 8302 | 0.23 W/m/K | |
| Deflection Temperature Under Load? | 1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距 9 | ISO 75-2/Ae | 80.0 °C |
| Linear thermal expansion coefficient | 横向 : -40 到 40°C | ASTM E831 | 1.1E-4 cm/cm/°C |
| Vicat Softening Temperature | -- | ASTM D152510 | 91.0 °C |
| -- | ISO 306/B120 | 96.0 °C | |
| Linear thermal expansion coefficient | 横向 : 23 到 60°C | ISO 11359-2 | 9.0E-5 cm/cm/°C |
| 流动 : -40 到 40°C | ASTM E831, ISO 11359-2 | 1.1E-4 cm/cm/°C | |
| 流动 : 23 到 60°C | ISO 11359-2 | 9.0E-5 cm/cm/°C | |
| Ball PressureTest | 85°C | IEC 60695-10-2 | 通过 |
| Linear thermal expansion coefficient | 横向 : -40°C | ISO 11359-2 | 1.1E-4 cm/cm/°C |
| Deflection Temperature Under Load? | 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 8 | ISO 75-2/Af | 78.0 °C |
| 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 75.0 °C | |
| 0.45 MPa, 未退火, 3.20 mm | ASTM D648 | 79.0 °C |
| Hardness | 测试条件 | 测试方法 | SABIC INNOVATIVE US/X8300MR |
|---|---|---|---|
| Shore Hardness | 邵氏 D, 10 秒 | ASTM D2240 | 73 |
| Injection | 测试条件 | 测试方法 | SABIC INNOVATIVE US/X8300MR |
|---|---|---|---|
| Middle Temperature | 240 到 260 °C | ||
| Drying Time | 3.0 到 5.0 hr | ||
| Suggested Shot Size | 40 到 80 % | ||
| Drying Temperature | 65 到 75 °C | ||
| Mold Temperature | 45 到 60 °C | ||
| Vent Depth | 0.013 到 0.020 mm | ||
| Suggested Max Moisture | 0.020 % | ||
| Processing (Melt) Temp | 245 到 265 °C | ||
| Rear Temperature | 240 到 250 °C | ||
| Nozzle Temperature | 245 到 265 °C | ||
| Front Temperature | 245 到 265 °C | ||
| Back Pressure | 0.200 到 0.500 Mpa | ||
| Screw Speed | 20 到 100 rpm |
| Physical | 测试条件 | 测试方法 | SABIC INNOVATIVE US/X8300MR |
|---|---|---|---|
| Melt Mass-Flow Rate | 265°C/2.16 kg | ASTM D1238 | 15 g/10 min |
| Moisture Absorption | 平衡, 23°C, 50% RH | ISO 62 | 0.20 % |
| Melt Volume flow Rate | 265°C/2.16 kg | ISO 1133 | 15.0 cm3/10min |
| Modeling Shrinkage | 横向流动 : 3.20 mm | 内部方法 | 0.40 到 0.60 % |
| 流动 : 3.20 mm | 内部方法 | 0.50 到 0.80 % | |
| Moisture Absorption | 饱和, 23°C | ISO 62 | 0.050 % |
| Mechanical Properties | 测试条件 | 测试方法 | SABIC INNOVATIVE US/X8300MR |
|---|---|---|---|
| Tensile Strength | 断裂 | ISO 527-2/50 | 54.0 Mpa |
| Tensile Modulus | -- | ISO 527-2/1 | 1600 Mpa |
| Tensile Elongation | 断裂 3 | ASTM D638 | 150 % |
| Tensile Strength | 屈服 3 | ASTM D638 | 47.0 Mpa |
| Tensile Elongation | 屈服 | ISO 527-2/50 | > 5.0 % |
| Flexural Modulus | 50.0 mm 跨距 4 | ASTM D790 | 1680 Mpa |
| Tensile Modulus | -- 2 | ASTM D638 | 1520 Mpa |
| Tensile Strength | 屈服 | ISO 527-2/50 | 55.0 Mpa |
| Flexural Stress | 屈服, 50.0 mm 跨距 4 | ASTM D790 | 71.0 Mpa |
| Tensile Elongation | 屈服 3 | ASTM D638 | 5.0 % |
| Flexural Stress | -- 5, 6 | ISO 178 | 78.0 Mpa |
| Flexural Modulus | -- 5 | ISO 178 | 1700 Mpa |
| Tensile Elongation | 断裂 | ISO 527-2/50 | > 200 % |
| Tensile Strength | 断裂 3 | ASTM D638 | 46.0 Mpa |
| Optical | 测试条件 | 测试方法 | SABIC INNOVATIVE US/X8300MR |
|---|---|---|---|
| Haze | 2540 µm | ASTM D1003 | 1.0 % |
| Index of Refraction | ISO 489 | 1.539 | |
| Transmittance | 2540 µm | ASTM D1003 | 88.0 % |
| Impact Properties | 测试条件 | 测试方法 | SABIC INNOVATIVE US/X8300MR |
|---|---|---|---|
| Instrumented Dart Impact | 23°C, Total Energy | ASTM D3763 | 95.0 J |
| Flammability | 测试条件 | 测试方法 | SABIC INNOVATIVE US/X8300MR |
|---|---|---|---|
| UL flame retardant rating | 3.0 mm | UL 94 | V-2 |
| Glow Wire Flammability Index | 1.0 mm | IEC 60695-2-12 | 750 °C |
| Electrical Properties | 测试条件 | 测试方法 | SABIC INNOVATIVE US/X8300MR |
|---|---|---|---|
| Volume Resistivity | ASTM D257 | > 1.0E+15 ohms·cm | |
| Surface Resistivity | ASTM D257 | > 1.0E+15 ohms | |
| Comparative Tracking Index | UL 746 | PLC 0 |