原料比对
产品信息
品名
品牌名
典型应用
特性
认证
PC/PET 5220U GY3A500 SABIC INNOVATIVE US
XYLEX™
Automotive Applications、Electronic and electrical
Flame retardant、High heat resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
物性数据
| Thermal Properties | 测试条件 | 测试方法 | SABIC INNOVATIVE US/5220U GY3A500 |
|---|---|---|---|
| RTI | UL 746 | 75.0 °C | |
| Deflection Temperature Under Load? | 1.8 MPa, 未退火, 6.40 mm | ASTM D648 | 99.0 °C |
| 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 10 | ISO 75-2/Af | 75.0 °C | |
| 0.45 MPa, 未退火, 6.40 mm | ASTM D648 | 107 °C | |
| Linear thermal expansion coefficient | 横向 : -40 到 40°C | ASTM E831 | 9.0E-5 cm/cm/°C |
| Vicat Softening Temperature | -- | ISO 306/B50 | 120 °C |
| -- | ISO 306/B120 | 125 °C | |
| RTI Elec | UL 746 | 75.0 °C | |
| Vicat Softening Temperature | -- | ASTM D152511 | 122 °C |
| Linear thermal expansion coefficient | 流动 : -40 到 40°C | ASTM E831, ISO 11359-2 | 9.5E-5 cm/cm/°C |
| 横向 : -40°C | ISO 11359-2 | 9.0E-5 cm/cm/°C | |
| RTI Imp | UL 746 | 75.0 °C | |
| Deflection Temperature Under Load? | 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 84.0 °C |
| Injection | 测试条件 | 测试方法 | SABIC INNOVATIVE US/5220U GY3A500 |
|---|---|---|---|
| Middle Temperature | 250 到 270 °C | ||
| Drying Time | 4.0 到 6.0 hr | ||
| Suggested Shot Size | 50 到 80 % | ||
| Drying Temperature | 110 °C | ||
| Mold Temperature | 65 到 90 °C | ||
| Vent Depth | 0.013 到 0.020 mm | ||
| Suggested Max Moisture | 0.020 % | ||
| Processing (Melt) Temp | 260 到 275 °C | ||
| Rear Temperature | 245 到 265 °C | ||
| Nozzle Temperature | 255 到 270 °C | ||
| Front Temperature | 255 到 275 °C | ||
| Back Pressure | 0.300 到 0.700 Mpa | ||
| Screw Speed | 50 到 80 rpm |
| Physical | 测试条件 | 测试方法 | SABIC INNOVATIVE US/5220U GY3A500 |
|---|---|---|---|
| Melt Mass-Flow Rate | 250°C/5.0 kg | ISO 1133 | 16 g/10 min |
| Moisture Absorption | 平衡, 23°C, 50% RH | ISO 62 | 0.15 % |
| Outdoor Suitability | UL 746C | f2 | |
| Modeling Shrinkage | 横向流动 2 | 内部方法 | 0.80 到 1.0 % |
| Melt Volume flow Rate | 250°C/5.0 kg | ISO 1133 | 15.0 cm3/10min |
| Specific Volume | ASTM D792 | 0.830 cm³/g | |
| Modeling Shrinkage | 流动 : 3.20 mm | 内部方法 | 0.80 到 1.0 % |
| Moisture Absorption | 饱和, 23°C | ISO 62 | 0.50 % |
| Mechanical Properties | 测试条件 | 测试方法 | SABIC INNOVATIVE US/5220U GY3A500 |
|---|---|---|---|
| Tensile Strength | 断裂 | ISO 527-2/50 | 50.0 Mpa |
| Tensile Modulus | -- | ISO 527-2/1 | 2050 Mpa |
| Tensile Elongation | 断裂 5 | ASTM D638 | 120 % |
| Flexural Stress | -- 7, 8 | ISO 178 | 80.0 Mpa |
| Tensile Elongation | 屈服 | ISO 527-2/50 | 4.0 % |
| Tensile Strength | 屈服 5 | ASTM D638 | 53.0 Mpa |
| Flexural Modulus | 50.0 mm 跨距 6 | ASTM D790 | 2030 Mpa |
| Tensile Strength | 屈服 | ISO 527-2/50 | 50.0 Mpa |
| Flexural Stress | 屈服, 50.0 mm 跨距 6 | ASTM D790 | 84.0 Mpa |
| Tensile Modulus | -- 3 | ASTM D638 | 2250 Mpa |
| -- 4 | ASTM D638 | 2250 Mpa | |
| Tensile Strength | 断裂 5 | ASTM D638 | 51.0 Mpa |
| Tensile Elongation | 屈服 5 | ASTM D638 | 4.0 % |
| Flexural Modulus | -- 7 | ISO 178 | 2000 Mpa |
| Tensile Elongation | 断裂 | ISO 527-2/50 | 120 % |
| Impact Properties | 测试条件 | 测试方法 | SABIC INNOVATIVE US/5220U GY3A500 |
|---|---|---|---|
| Instrumented Dart Impact | 23°C, Total Energy | ASTM D3763 | 60.0 J |
| Flammability | 测试条件 | 测试方法 | SABIC INNOVATIVE US/5220U GY3A500 |
|---|---|---|---|
| UL flame retardant rating | 1.5 mm | UL 94 | HB |
| Electrical Properties | 测试条件 | 测试方法 | SABIC INNOVATIVE US/5220U GY3A500 |
|---|---|---|---|
| Hot-wire Ignition | UL 746 | PLC 3 | |
| Arc Resistance | ASTM D495 | PLC 5 | |
| Comparative Tracking Index | UL 746 | PLC 1 | |
| High Amp Arc Ignition | UL 746 | PLC 0 | |
| High Voltage Arc Tracking Rate | UL 746 | PLC 0 |