PA6 PX11313-WH5G004 SABIC INNOVATIVE US
LNP™ KONDUIT™
Lighting applications、Electronic and Electrical、Plastic bag
Non chloro non bromine fl、heat conduction
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
物性数据
| Thermal Properties | 测试条件 | 测试方法 | SABIC INNOVATIVE US/PX11313-WH5G004 |
|---|---|---|---|
| RTI | UL 746 | 120 °C | |
| Deflection Temperature Under Load? | 1.8 MPa, 未退火, 6.40 mm | ASTM D648 | 215 °C |
| Linear thermal expansion coefficient | 横向 : 40 到 120°C | ASTM E831 | 8.5E-5 cm/cm/°C |
| RTI Elec | UL 746 | 130 °C | |
| Thermal Conductivity | -- 11 | ISO 22007-2 | 0.90 W/m/K |
| -- 12 | ISO 22007-2 | 1.9 W/m/K | |
| -- 10 | ASTM E1461 | 1.8 W/m/K | |
| Deflection Temperature Under Load? | 0.45 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 8 | ISO 75-2/Bf | 228 °C |
| 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 8 | ISO 75-2/Af | 208 °C | |
| Ball PressureTest | 123 到 127°C | IEC 60695-10-2 | 通过 |
| RTI Imp | UL 746 | 105 °C | |
| Linear thermal expansion coefficient | 流动 : 40 到 120°C | ASTM E831 | 4.1E-5 cm/cm/°C |
| Deflection Temperature Under Load? | 0.45 MPa, 未退火, 3.20 mm | ASTM D648 | 227 °C |
| Thermal Conductivity | -- 9 | ASTM E1461 | 1.4 W/m/K |
| Injection | 测试条件 | 测试方法 | SABIC INNOVATIVE US/PX11313-WH5G004 |
|---|---|---|---|
| Suggested Max Moisture | 0.15 到 0.25 % | ||
| Middle Temperature | 270 到 290 °C | ||
| Processing (Melt) Temp | 270 到 295 °C | ||
| Drying Time | 4.0 hr | ||
| Rear Temperature | 260 到 275 °C | ||
| Drying Temperature | 80 °C | ||
| Front Temperature | 270 到 290 °C | ||
| Back Pressure | 0.200 到 0.300 Mpa | ||
| Mold Temperature | 85 到 100 °C | ||
| Screw Speed | 20 到 60 rpm |
| Physical | 测试条件 | 测试方法 | SABIC INNOVATIVE US/PX11313-WH5G004 |
|---|---|---|---|
| Modeling Shrinkage | 流动 : 24小时 | ASTM D955 | 0.42 % |
| Moisture Absorption | 平衡, 23°C, 50% RH | ISO 62 | 0.040 % |
| Modeling Shrinkage | 横向流动 : 24小时 | ASTM D955 | 0.58 % |
| Moisture Absorption | 24 hr, 23°C | ISO 62 | 0.040 % |
| 24 hr, 23°C 2 | ISO 62 | 0.23 % |
| Mechanical Properties | 测试条件 | 测试方法 | SABIC INNOVATIVE US/PX11313-WH5G004 |
|---|---|---|---|
| Tensile Modulus | -- | ISO 527-2/1 | 13300 Mpa |
| Flexural Stress | 屈服, 50.0 mm 跨距 5 | ASTM D790 | 167 Mpa |
| Tensile Modulus | -- 3 | ASTM D638 | 13300 Mpa |
| Tensile Elongation | 断裂 | ISO 527-2/5 | 1.3 % |
| Flexural Stress | 断裂, 50.0 mm 跨距 5 | ASTM D790 | 176 Mpa |
| Tensile Elongation | 断裂 4 | ASTM D638 | 1.3 % |
| Flexural Stress | -- 6, 7 | ISO 178 | 186 Mpa |
| Tensile Strength | 断裂 | ISO 527-2/5 | 108 Mpa |
| Flexural Modulus | -- 6 | ISO 178 | 13000 Mpa |
| Tensile Strength | 断裂 4 | ASTM D638 | 98.0 Mpa |
| Flexural Modulus | 50.0 mm 跨距 5 | ASTM D790 | 12500 Mpa |
| Impact Properties | 测试条件 | 测试方法 | SABIC INNOVATIVE US/PX11313-WH5G004 |
|---|---|---|---|
| Unnotched Izod Impact Strength | 23°C | ASTM D4812 | 330 J/m |
| 23°C 8 | ISO 180/1U | 23 kJ/m² |
| Flammability | 测试条件 | 测试方法 | SABIC INNOVATIVE US/PX11313-WH5G004 |
|---|---|---|---|
| Glow Wire Ignition Temperature | 1.0 mm | IEC 60695-2-13 | 750 °C |
| Glow Wire Flammability Index | 1.0 到 3.0 mm | IEC 60695-2-12 | 960 °C |
| UL flame retardant rating | 0.8 mm | UL 94 | V-0 |
| Glow Wire Ignition Temperature | 3.0 mm | IEC 60695-2-13 | 800 °C |
| Electrical Properties | 测试条件 | 测试方法 | SABIC INNOVATIVE US/PX11313-WH5G004 |
|---|---|---|---|
| Hot-wire Ignition | UL 746 | PLC 3 | |
| Dissipation Factor? | 1.10 GHz | ASTM ES7-83 | 9.9E-3 |
| Dielectric Strength | 1.00 mm, in Oil | ASTM D149 | > 10 KV/mm |
| Surface Resistivity | ASTM D257 | > 1.0E+15 ohms | |
| High Amp Arc Ignition | UL 746 | PLC 0 | |
| Dielectric Constant | 1.10 GHz | ASTM ES7-83 | 4.84 |
| Comparative Tracking Index | IEC 60112 | 600 V |