ASA/PC HRA222F-GY6G053 SABIC INNOVATIVE NANSHA
GELOY™
Home appliance components、Lawn garden equipment
High temperature resistan、Thermal stability
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
物性数据
| Thermal Properties | 测试条件 | 测试方法 | SABIC INNOVATIVE NANSHA/HRA222F-GY6G053 |
|---|---|---|---|
| RTI | UL 746 | 90.0 °C | |
| Heat Deflection Temperature | 1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距 | ISO 75-2/Ae | 88.0 °C |
| Vicat Softening Temperature | -- | ISO 306/B50 | 102 °C |
| -- | ISO 306/B120 | 104 °C | |
| RTI Imp | UL 746 | 90.0 °C | |
| Ball PressureTest | 73 到 77°C | IEC 60695-10-2 | 通过 |
| RTI Elec | UL 746 | 90.0 °C | |
| Heat Deflection Temperature | 0.45 MPa, 未退火, 4.00 mm, 100 mm 跨距 | ISO 75-2/Be | 99.0 °C |
| Vicat Softening Temperature | -- | ISO 306/A50 | 111 °C |
| Linear thermal expansion coefficient | 横向 : -30 到 80°C | ISO 11359-2 | 7.1E-5 cm/cm/°C |
| 横向 : 23 到 80°C | ISO 11359-2 | 7.5E-5 cm/cm/°C | |
| 流动 : -30 到 80°C | ISO 11359-2 | 6.9E-5 cm/cm/°C |
| Injection | 测试条件 | 测试方法 | SABIC INNOVATIVE NANSHA/HRA222F-GY6G053 |
|---|---|---|---|
| Suggested Max Moisture | 0.020 % | ||
| Middle Temperature | 220 到 260 °C | ||
| Processing (Melt) Temp | 230 到 270 °C | ||
| Drying Time | 2.0 到 4.0 hr | ||
| Rear Temperature | 200 到 230 °C | ||
| Nozzle Temperature | 220 到 260 °C | ||
| Drying Temperature | 80 到 90 °C | ||
| Front Temperature | 230 到 270 °C | ||
| Hopper Temperature | 60 到 80 °C | ||
| Mold Temperature | 50 到 70 °C |
| Physical | 测试条件 | 测试方法 | SABIC INNOVATIVE NANSHA/HRA222F-GY6G053 |
|---|---|---|---|
| Moisture Absorption | 平衡, 23°C, 50% RH | ISO 62 | 0.20 % |
| Modeling Shrinkage - Flow | 内部方法 | 0.40 到 0.60 % | |
| Outdoor Suitability | UL 746C | f1 | |
| Moisture Absorption | 饱和, 23°C | ISO 62 | 0.60 % |
| Melt Volume flow Rate | 260°C/2.16 kg | ISO 1133 | 13.0 cm3/10min |
| Mechanical Properties | 测试条件 | 测试方法 | SABIC INNOVATIVE NANSHA/HRA222F-GY6G053 |
|---|---|---|---|
| Tensile Strength | 断裂 | ISO 527-2/50 | 45.0 Mpa |
| Tensile Modulus | -- | ISO 527-2/1 | 2520 Mpa |
| Tensile Elongation | 断裂 5 | ASTM D638 | > 100 % |
| 断裂 4 | ASTM D638 | > 100 % | |
| Tensile Strength | 断裂 | ISO 527-2/5 | 51.0 Mpa |
| Flexural Modulus | ISO 178 | 2510 Mpa | |
| Tensile Elongation | 屈服 | ISO 527-2/50 | 4.4 % |
| Tensile Strength | 屈服 5 | ASTM D638 | 59.0 Mpa |
| 屈服 4 | ASTM D638 | 63.0 Mpa | |
| Tensile Elongation | 断裂 | ISO 527-2/5, ISO 527-2/50 | > 50 % |
| Tensile Strength | 屈服 | ISO 527-2/50 | 60.0 Mpa |
| Tensile Elongation | 屈服 | ISO 527-2/5 | 4.3 % |
| Tensile Modulus | -- 3 | ASTM D638 | 2590 Mpa |
| Tensile Strength | 断裂 5 | ASTM D638 | 66.0 Mpa |
| 断裂 4 | ASTM D638 | 56.0 Mpa | |
| 屈服 | ISO 527-2/5 | 62.0 Mpa | |
| Tensile Elongation | 屈服 5 | ASTM D638 | 4.2 % |
| 屈服 4 | ASTM D638 | 4.3 % | |
| Flexural Stress | ISO 178 | 93.0 Mpa |
| Flammability | 测试条件 | 测试方法 | SABIC INNOVATIVE NANSHA/HRA222F-GY6G053 |
|---|---|---|---|
| UL flame retardant rating | 2.0 mm | UL 94 | V-0 |
| Oxygen Index | ISO 4589-2 | 29 % |
| Electrical Properties | 测试条件 | 测试方法 | SABIC INNOVATIVE NANSHA/HRA222F-GY6G053 |
|---|---|---|---|
| Comparative Tracking Index | UL 746 | PLC 0 | |
| IEC 60112 | 600 V |