LLDPE 2049G 西班牙陶氏
DOWLEX™ 
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

物性数据

热性能测试条件测试方法西班牙陶氏/2049G
熔融温度Internal Method121 °C
维卡软化温度ASTM D1525112 °C
ASTM D-1525112 °C
其它性能测试条件测试方法西班牙陶氏/2049G
薄膜穿刺强度38.1umInternal Method3.06 J/cm³
薄膜韧性38.1um，TDASTM D-882140 J/cm³
38.1um，MDASTM D-882128 J/cm4
机械性能测试条件测试方法西班牙陶氏/2049G
埃尔曼多夫撕裂强度38.1um，TDASTM D-1922590 g
38.1um，MDASTM D-1922250
断裂伸长率38.1um，MDASTM D-882630 %
38.1um，TDASTM D-882740 %
割线模量2% Secant，38.1um，MDASTM D-882235 Mpa
2% Secant，38.1um，TDASTM D-882281 Mpa
拉伸强度38.1um，MD,断裂ASTM D-88247.8 Mpa
38.1um，屈服,TDASTM D-88214.7 Mpa
38.1um，TD,断裂ASTM D-88242.3 Mpa
38.1um，屈服,MDASTM D-88213.2 Mpa
落镖冲击25.4umASTM D-1709A220 g
薄膜测试条件测试方法西班牙陶氏/2049G
埃尔曼多夫撕裂强度MD:38µmASTM D1922250 g
TD:38µmASTM D1922590 g
薄膜穿刺强度38µmInternal Method3.06 J/cm³
薄膜厚度38 µm
割线模量2%正割,TD:38µmASTM D882281 Mpa
2%正割,MD:38µmASTM D882235 Mpa
拉伸强度TD:断裂,38µmASTM D88242.3 Mpa
MD:断裂,38µmASTM D88247.8 Mpa
MD:屈服,38µmASTM D88213.2 Mpa
TD:屈服,38µmASTM D88214.7 Mpa
落镖冲击25µmASTM D1709A220 g
膜强度TD:38µmASTM D882140 J/cm³
MD:38µmASTM D882128 J/cm³
伸长率MD:断裂,38µmASTM D882630 %
TD:断裂,38µmASTM D882740 %
基本性能测试条件测试方法西班牙陶氏/2049G
薄膜厚度38.1 um
密度ASTM D-7920.926 g/m3
熔体质量流动速率ASTM D-12381 g/10min
加工性能测试条件测试方法西班牙陶氏/2049G
熔体温度207-216 °C
光学性能测试条件测试方法西班牙陶氏/2049G
光泽度45°，38.1umASTM D-245780
45°,38.1µmASTM D245780
雾度38.1µmASTM D10039.0 %
38.1umASTM D-10039 %
物理性能测试条件测试方法西班牙陶氏/2049G
密度ASTM D7920.926 g/cm³
熔体质量流动速率190°C/2.16kgASTM D12381.0 g/10min