PC+AS(SAN) LNP™ LUBRILOY™ Lexan_WR6300 compound SABIC

Mô tả sản phẩm

Chứng nhận(0)

Bảng tính chất

Mô tả sản phẩm

Chứng nhận

No Data...

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra	Đơn vị kiểm tra
Impact strength of cantilever beam gap	-30°C	ASTM D256	170	J/m
	Impact strength of cantilever beam gap	23°C	ASTM D256	680	J/m
		Impact strength of cantilever beam gap	-30°C	ASTM D256	170	J/m
			Impact strength of cantilever beam gap	23°C	ASTM D256	680	J/m
			Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ASTM D4812	2500	J/m
Dart impact	23°C,TotalEnergy	ASTM D3763	60.2	J
Suspended wall beam without notch impact strength	23°C	ASTM D4812	2500	J/m
Dart impact	23°C,TotalEnergy	ASTM D3763	60.2	J
flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra	Đơn vị kiểm tra
UL flame retardant rating	1.5mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	1.50mm	UL 94	HB
mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra	Đơn vị kiểm tra
tensile strength	Yield	ASTM D638	60.7	MPa
tensile strength	tensile strength	Break	ASTM D638	61.4	MPa
elongation	Break	ASTM D638	160	%
Bending modulus	50.0mmSpan	ASTM D790	2490	MPa
bending strength	Yield,50.0mmSpan	ASTM D790	96.5	MPa
tensile strength	Yield	ASTM D638	60.7	MPa
tensile strength	tensile strength	Break	ASTM D638	61.4	MPa
elongation	Break	ASTM D638	160	%
Bending modulus	50.0mmSpan	ASTM D790	2490	MPa
bending strength	Yield,50.0mmSpan	ASTM D790	96.5	MPa
thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra	Đơn vị kiểm tra
Vicat softening temperature		ASTM D15254	137	°C
Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	1.1E-04	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：-40to40°C	ASTME831	1.2E-04	cm/cm/°C
Hot deformation temperature	0.45MPa,Unannealed,6.40mm	ASTM D648	134	°C
	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	117	°C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	121	°C
RTI Str		UL 746	80.0	°C
Hot deformation temperature	0.45MPa,Unannealed,6.40mm	ASTM D648	134	°C
	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	117	°C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	121	°C
RTI Elec		UL 746	80.0	°C
RTI Imp		UL 746	80.0	°C
Vicat softening temperature		ASTM D15255	137	°C
Linear coefficient of thermal expansion	MD:-40to40°C	ASTME831	1.1E-04	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD:-40to40°C	ASTME831	1.2E-04	cm/cm/°C
RTI Elec		UL 746	80.0	°C
RTI Imp		UL 746	80.0	°C
RTI		UL 746	80.0	°C
Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra	Đơn vị kiểm tra
Shrinkage rate	MD：3.20mm	Internal Method	0.50to0.70	%
density		ASTM D792	1.17	g/cm³
Melt Volume Flow Rate (MVR)	300°C/2.16kg	ISO 1133	38.0	cm³/10min
Shrinkage rate	MD：3.20mm	Internal Method	0.50to0.70	%
density		ASTM D792	1.17	g/cm³
Melt Volume Flow Rate (MVR)	300°C/2.16kg	ISO 1133	38.0	cm³/10min

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.