mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra	Đơn vị kiểm tra
tensile strength	Yield	ISO 178	35	Mpa
	tensile strength	Type I, 50 mm/min，Yield	ASTM D638	45	Mpa
		tensile strength	Yield	ISO 178	55	Mpa
		tensile strength	tensile strength	Type I, 50 mm/min，Yield	ASTM D638	58	Mpa
Elongation at Break	Break	ISO 178	30	%
Elongation at Break	Elongation at Break	Type I, 50 mm/min，Break	ASTM D638	32	%
elongation at yield		ISO 178	3.8	%
elongation at yield	elongation at yield	Type I, 50 mm/min	ASTM D638	4	%
Tensile modulus		GB/T 15585-1995	5.2
Tensile modulus	Tensile modulus		1 mm/min; ISO 527	5.58
bending strength	1.3 mm/min, 50 mm span	ASTM D790	98	Mpa
bending strength	bending strength		2 mm/min; ISO 178	99	Mpa
Bending modulus	1.3 mm/min, 50 mm span	ASTM D790	4.53
Bending modulus	Bending modulus		2 mm/min; ISO 178	4.58
Impact strength of cantilever beam gap		ASTM D256	0.69	J/cm
	Impact strength of cantilever beam gap		ASTM D256	0.55	J/cm
		Impact strength of cantilever beam gap			@Temperature -30.0
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		80104; ISO 180/1A	5	kJ/m²
Charpy Notched Impact Strength		Edgew 80104 sp=62mm; ISO 179/1eA	0.5	J/cm²
thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra	Đơn vị kiểm tra
Linear coefficient of thermal expansion	Flow	GB 1040	42	µm/m-°C
	Linear coefficient of thermal expansion	Flow	ISO 11359-2	42	µm/m-°C
		Linear coefficient of thermal expansion	Across Flow	GB 1040	49	µm/m-°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow	ISO 11359-2	59	µm/m-°C
Hot deformation temperature	1.8 MPa	Flatw 80104 sp=64mm; ISO 75/Af	89
Hot deformation temperature	Hot deformation temperature	1.8 MPa	ASTMF1249	88
Vicat softening temperature		Rate B/50; ISO 306	107
	Vicat softening temperature		Rate B/50; ASTM D1525	108
	Vicat softening temperature	Vicat softening temperature		Equate	110
UL flame retardant rating		UL 94	V-0
Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra	Đơn vị kiểm tra
Water absorption rate		23°C / 50% RH; ISO 62	0.04	%
Water absorption rate	Water absorption rate	Saturation	ISO 62	0.09	%
Shrinkage rate	Flow	SABIC method	0.0025 - 0.0035	cm/cm
melt mass-flow rate		ASTM D1238	13
melt mass-flow rate	melt mass-flow rate		ASTM D1238	@Load 2.16 kg. Temperature 260
Compound melt index		MVR [cm^3/10 min]; ISO 1133	49.0 µm/m-°C	g/10 min
Compound melt index	Compound melt index			@Load 2.16 kg. Temperature 260

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.