Ethylene Copolymer Generic EVA Generic

Mô tả sản phẩm

Chứng nhận(0)

Bảng tính chất

Mô tả sản phẩm

Chứng nhận

No Data...

Bảng thông số kỹ thuật

	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra	Đơn vị kiểm tra
melt mass-flow rate	190°C/2.16kg	ASTM D1238	0.15to20	g/10min
melt mass-flow rate	melt mass-flow rate	190°C/2.16kg	ISO 1133	0.30to20	g/10min
Environmental stress cracking resistance	23°C	ASTM D1693	1.00to300	hr
Vinyl acetate content			8.4to33.1	wt%
Shore hardness	23°C	ASTM D2240	14to98
Shore hardness	Shore hardness	23°C	ISO 868	30to96
Tensile modulus	23°C	ASTM D638	3.00to91.3	MPa
Bending modulus	23°C	ASTM D747	29.4to98.1	MPa
Dart impact	23°C	ASTM D1709	70to740	g
Dart impact	Dart impact	23°C	ISO 7765-1	420to720	g
Elmendorf tear strength	MD	ASTM D1922	12to250	g
Melting temperature	--	ISO 3146	68.5to101	°C
gloss		ASTM D2457	29to92
turbidity		ASTM D1003	0.70to8.1	%
Permanent compression deformation		ASTM D395	18to68	%
Dart impact	23°C	ASTM D3763	14.6to21.7	J
Impact strength of cantilever beam gap	23°C	ISO 8256	225	kJ/m²
Brittle temperature		ASTM D746	-81.3--69.3	°C
film thickness			30to64	µm
Secant modulus	MD	ASTM D882	33.5to149	MPa
	Secant modulus	TD	ASTM D882	36.6to125	MPa
	Secant modulus	Secant modulus	23°C	ISO 527-3	5.00to128	MPa
tensile strength	MD:Yield	ASTM D882	2.50to41.0	MPa
tensile strength	tensile strength	TD:Yield	ASTM D882	3.63to30.3	MPa
Elmendorf tear strength	TD	ASTM D1922	45to260	g
Elmendorf tear strength	Elmendorf tear strength	--	ISO 6383-2	2.0to13	N
Bending modulus	23°C	ASTM D790	2.00to64.4	MPa
Bending modulus	Bending modulus	23°C	ISO 178	10.0to400	MPa
bending strength	Yield,23°C	ASTM D790	40.0to164	MPa
Friction coefficient		ASTM D1894	0.49to0.50
density	--	ASTM D792	0.914to0.982	g/cm³
	density	23°C	ISO 1183	0.922to0.967	g/cm³
	density	density	--	ASTM D1505	0.920to0.958	g/cm³
Glass transition temperature		ASTME1356	-32.0-0.175	°C
Vicat softening temperature	--	ASTM D1525	38.6to82.8	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306	38.7to85.6	°C
Melting temperature	--		58.8to105	°C
	Melting temperature	--	DSC	65.8to113	°C
	Melting temperature	Melting temperature	--	ASTM D3418	58.3to103	°C
Tensile modulus	23°C	ISO 527-2	50.0to115	MPa
tensile strength	Yield,23°C	ASTM D638	2.71to18.0	MPa
	tensile strength	Yield,23°C	ISO 527-2	2.70to7.08	MPa
		tensile strength	Break,23°C	ASTM D638	1.38to20.3	MPa
			tensile strength	Break,23°C	ISO 527-2	2.00to26.6	MPa
				tensile strength	23°C	ASTM D638	1.90to8.20	MPa
				tensile strength	tensile strength	23°C	ISO 527-2	3.96to10.0	MPa
elongation	Break,23°C	ASTM D638	90to920	%
elongation	elongation	Break,23°C	ISO 527-2	380to1000	%
tensile strength	Yield,23°C	ISO 527-3	4.00to8.25	MPa
	tensile strength	MD:Break	ASTM D882	14.7to33.7	MPa
		tensile strength	TD:Break	ASTM D882	4.30to36.8	MPa
			tensile strength	Break,23°C	ISO 527-3	22.0to39.0	MPa
			tensile strength	tensile strength	23°C	ISO 527-3	15.0to27.1	MPa
elongation	MD:Yield	ASTM D882	9.0to410	%
	elongation	TD:Yield	ASTM D882	9.0to560	%
		elongation	MD:Break	ASTM D882	170to720	%
			elongation	TD:Break	ASTM D882	480to800	%
			elongation	elongation	Break,23°C	ISO 527-3	300to900	%

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.