PC+PET XYLEX™ X2500UV resin SABIC

Mô tả sản phẩm

Chứng nhận(0)

Bảng tính chất

Mô tả sản phẩm

Chứng nhận

No Data...

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra	Đơn vị kiểm tra
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	无断裂
Impact strength of cantilever beam gap	-30°C	ASTM D256	200	J/m
	Impact strength of cantilever beam gap	0°C	ASTM D256	450	J/m
		Impact strength of cantilever beam gap	23°C	ASTM D256	600	J/m
			Impact strength of cantilever beam gap	-40°C9	ISO 180/1A	15	kJ/m²
				Impact strength of cantilever beam gap	-30°C9	ISO 180/1A	25	kJ/m²
				Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C9	ISO 180/1A	40	kJ/m²
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	30	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	50	kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	无断裂
Impact strength of cantilever beam gap	-30°C	ASTM D256	200	J/m
	Impact strength of cantilever beam gap	0°C	ASTM D256	450	J/m
		Impact strength of cantilever beam gap	23°C	ASTM D256	600	J/m
			Impact strength of cantilever beam gap	-40°C10	ISO 180/1A	15	kJ/m²
				Impact strength of cantilever beam gap	-30°C10	ISO 180/1A	25	kJ/m²
				Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C10	ISO 180/1A	40	kJ/m²
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	无断裂
Dart impact	23°C,TotalEnergy	ASTM D3763	60.0	J
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	无断裂
Dart impact	23°C,TotalEnergy	ASTM D3763	60.0	J
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	30	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	50	kJ/m²
flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra	Đơn vị kiểm tra
UL flame retardant rating	1.5mm	UL 94	HB
Burning wire flammability index	2.7mm	IEC 60695-2-12	750	°C
Burning wire flammability index	Burning wire flammability index	2.7mm	IEC 60695-2-12	750	°C
UL flame retardant rating	1.5mm	UL 94	HB
mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra	Đơn vị kiểm tra
Tensile modulus	--	ISO 527-2/1	2200	MPa
tensile strength	Yield	ASTM D638	53.0	MPa
	tensile strength	Yield4	ASTM D638	56.0	MPa
		tensile strength	Yield	ISO 527-2/50	57.0	MPa
			tensile strength	Break4	ASTM D638	55.0	MPa
			tensile strength	tensile strength	Break	ISO 527-2/50	56.0	MPa
elongation	Yield	ASTMD638	5.0	%
	elongation	Yield4	ASTM D638	5.0	%
		elongation	Break	ASTM D638	100	%
		elongation	elongation	Break4	ASTM D638	80	%
tensile strength	Break5	ASTM D638	55.0	MPa
tensile strength	tensile strength	Break	ISO 527-2/50	56.0	MPa
elongation	Yield	ASTMD638	5.0	%
	elongation	Yield5	ASTM D638	5.0	%
		elongation	Break	ASTM D638	100	%
			elongation	Break5	ASTM D638	80	%
			elongation	elongation	Break	ISO 527-2/50	70	%
Bending modulus	--	ASTM D790	2100	MPa
	Bending modulus	50.0mmSpan6	ASTM D790	2150	MPa
	Bending modulus	Bending modulus	--7	ISO 178	2150	MPa
elongation	Break	ISO 527-2/50	70	%
Bending modulus	50.0mmSpan5	ASTM D790	2150	MPa
	Bending modulus	--	ASTM D790	2100	MPa
	Bending modulus	Bending modulus	--6	ISO 178	2150	MPa
bending strength	--	ASTM D790	79.0	MPa
	bending strength	--6,7	ISO 178	80.0	MPa
	bending strength	bending strength	Yield,50.0mmSpan5	ASTM D790	79.0	MPa
Taber abraser	1000Cycles,1000g,CS-17Wheel	Internal Method	20.0	mg
Tensile modulus	--4	ASTM D638	2200	MPa
Tensile modulus	Tensile modulus	--	ISO 527-2/1	2200	MPa
tensile strength	Yield	ASTM D638	53.0	MPa
	tensile strength	Yield5	ASTM D638	56.0	MPa
	tensile strength	tensile strength	Yield	ISO 527-2/50	57.0	MPa
Tensile modulus	--3	ASTM D638	2200	MPa
bending strength	--	ASTM D790	79.0	MPa
	bending strength	--7,8	ISO 178	80.0	MPa
	bending strength	bending strength	Yield,50.0mmSpan6	ASTM D790	79.0	MPa
Taber abraser	1000Cycles,1000g,CS-17Wheel	Internal Method	20.0	mg
thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra	Đơn vị kiểm tra
Linear coefficient of thermal expansion	MD:23to80°C	ISO 11359-2	8.2E-05	cm/cm/°C
	Linear coefficient of thermal expansion	TD:-40to40°C	ASTME831	8.5E-05	cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD:23to80°C	ISO 11359-2	8.7E-05	cm/cm/°C
thermal conductivity		ISO 8302	0.18	W/m/K
Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan11	ISO 75-2/Af	108	°C
Vicat softening temperature	--	ASTMD152512	135	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/A50	145	°C
Linear coefficient of thermal expansion	TD:23to80°C	ISO 11359-2	8.7E-05	cm/cm/°C
thermal conductivity		ISO 8302	0.18	W/m/K
Hot deformation temperature	0.45MPa,Unannealed,64.0mmSpan11	ISO 75-2/Bf	126	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	108	°C
Vicat softening temperature	--	ISO 306/B120	136	°C
Ball Pressure Test	125°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	MD:-40to40°C	ASTME831	8E-05	cm/cm/°C
	Linear coefficient of thermal expansion	MD:23to80°C	ISO 11359-2	8.2E-05	cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD:-40to40°C	ASTME831	8.5E-05	cm/cm/°C
Hot deformation temperature	0.45MPa,Unannealed,64.0mmSpan10	ISO 75-2/Bf	126	°C
	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	108	°C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan10	ISO 75-2/Af	108	°C
Vicat softening temperature	--	ASTMD152511	135	°C
	Vicat softening temperature	--	ISO 306/A50	145	°C
	Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	136	°C
Ball Pressure Test	125°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	MD:-40to40°C	ASTME831	8E-05	cm/cm/°C
Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra	Đơn vị kiểm tra
melt mass-flow rate	265°C/2.16kg	ASTM D1238	9.0	g/10min
Melt Volume Flow Rate (MVR)	265°C/1.2kg	ISO 1133	4.00	cm³/10min
Shrinkage rate	MD3	Internal Method	0.50to0.80	%
	Shrinkage rate	MD:3.20mm	Internal Method	0.50to0.80	%
	Shrinkage rate	Shrinkage rate	TD3	Internal Method	0.50to0.80	%
Water absorption rate	Saturation,23°C	ISO 62	0.70	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.20	%
Shrinkage rate	MD:3.20mm	Internal Method	0.50to0.80	%
Shrinkage rate	Shrinkage rate	TD2	Internal Method	0.50to0.80	%
Water absorption rate	Saturation,23°C	ISO 62	0.70	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.20	%
density		ASTMD792	1.21	g/cm³
density	density		ASTMD792	1.21	g/cm³
melt mass-flow rate	265°C/2.16kg	ASTM D1238	9.0	g/10min
Melt Volume Flow Rate (MVR)	265°C/1.2kg	ISO 1133	4.00	cm³/10min
Shrinkage rate	MD2	Internal Method	0.50to0.80	%
Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra	Đơn vị kiểm tra
Dissipation factor	1MHz	IEC 60250	0.020
Surface resistivity		IEC 60093	>1.0E+15	ohms
Volume resistivity		IEC 60093	>1.0E+14	ohms·cm
Dielectric strength	3.20mm,in Oil	IEC 60243-1	17	kV/mm
Relative permittivity	50Hz	IEC 60250	3.30
	Relative permittivity	60Hz	IEC 60250	3.30
	Relative permittivity	Relative permittivity	1MHz	IEC 60250	3.10
Dissipation factor	50Hz	IEC 60250	2E-03
	Dissipation factor	60Hz	IEC 60250	2E-03
	Dissipation factor	Dissipation factor	1MHz	IEC 60250	0.020
Surface resistivity		IEC 60093	>1.0E+15	ohms
Volume resistivity		IEC 60093	>1.0E+14	ohms·cm
Dielectric strength	3.20mm,in Oil	IEC 60243-1	17	kV/mm
Relative permittivity	50Hz	IEC 60250	3.30
	Relative permittivity	60Hz	IEC 60250	3.30
	Relative permittivity	Relative permittivity	1MHz	IEC 60250	3.10
Dissipation factor	50Hz	IEC 60250	2E-03
Dissipation factor	Dissipation factor	60Hz	IEC 60250	2E-03
hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra	Đơn vị kiểm tra
Ball Pressure Test	H358/30	ISO 2039-1	95.0	MPa
Ball Pressure Test	Ball Pressure Test	H358/30	ISO 2039-1	95.0	MPa

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.