Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt Mass-Flow Rate | 300°C/1.2kg | ISO1133 | 10 | g/10min |
| Melt Volume flow Rate | 300°C/1.2kg | ISO1133 | 9.00 | cm3/10min |
| Modeling Shrinkage | TD:3.20mm | | 0.40to0.60 | % |
| Modeling Shrinkage | MD:3.20mm | | 0.30to0.50 | % |
| Moisture Absorption | 饱和,23°C | ISO62 | 0.14 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Modulus | | ISO527-2 | 4500 | Mpa |
| Tensile Stress | 断裂 | ISO527-2 | 78.0 | Mpa |
| Tensile Strain | 断裂 | ISO527-2 | 2.9 | % |
| Flexural Modulus | | ISO178 | 4000 | Mpa |
| Flexural Stress | | ISO178 | 135 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO75-2/B | 145 | °C |
| Heat Deflection Temperature | 1.8MPa,未退火 | ISO75-2/A | 140 | °C |
| Coefficient of Linear Thermal Expansion | MD | ISO11359-2 | 4E-05 | cm/cm/°C |
| Coefficient of Linear Thermal Expansion | TD | ISO11359-2 | 6.7E-05 | cm/cm/°C |
| Electrical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Comparative Tracking Index | CTI | UL746 | PLC4 | |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Unnotched Impact Strength | 23°C | ISO179 | 55 | kJ/m² |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Flame Rating | 0.75mm | UL94 | V-0 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare
View Prices