PBT VALOX™ V4860HR BK1066 SABIC INNOVATIVE JAPAN
38
- Properties:Glass fiber reinforcedDimensional stability
- Usages:Automotive ApplicationsLighting fixtures
Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Density / Specific Gravity | ASTMD792 | 1.64 | g/cm³ | |
ISO1183 | 1.64 | g/cm³ | ||
Moisture Absorption | 平衡,23°C,50%RH | ISO62 | 0.060 | % |
饱和,23°C | ISO62 | 0.19 | % | |
Modeling Shrinkage | TD:3.20mm | 内部方法 | 0.50to1.0 | % |
MD:3.20mm | 内部方法 | 0.50to0.70 | % | |
Melt Volume flow Rate | 250°C/5.0kg | ISO1133 | 12.4 | cm3/10min |
Melt Mass-Flow Rate | 250°C/5.0kg | ASTMD1238 | 18 | g/10min |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Tensile Stress | 断裂 | ISO527-2/5 | 111 | Mpa |
Tensile Elongation | 屈服 | ASTMD638 | 2.3 | % |
Tensile Strain | 屈服 | ISO527-2/5 | 2.1 | % |
Tensile Elongation | 断裂 | ASTMD638 | 2.3 | % |
Tensile Strain | 断裂 | ISO527-2/5 | 2.2 | % |
Flexural Modulus | 50.0mm跨距 | ASTMD790 | 6740 | Mpa |
ISO178 | 7880 | Mpa | ||
Flexural Stress | --6 | ISO178 | 182 | Mpa |
--7 | ISO178 | 183 | Mpa | |
Tensile Strength | 断裂 | ASTMD638 | 115 | Mpa |
Tensile Stress | 屈服 | ISO527-2/5 | 112 | Mpa |
Tensile Strength | 屈服 | ASTMD638 | 116 | Mpa |
Tensile Modulus | ISO527-2/1 | 9450 | Mpa | |
ASTMD638 | 9750 | Mpa | ||
Flexural Strength | 屈服,50.0mm跨距 | ASTMD790 | 174 | Mpa |
断裂,50.0mm跨距 | ASTMD790 | 2.96 | Mpa | |
Flexural Strain (Break) | ISO178 | 2.9 | % |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Heat Deflection Temperature | 1.8MPa,未退火,3.20mm | ASTMD648 | 197 | °C |
1.8MPa,未退火,6.40mm | ASTMD648 | 205 | °C | |
1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 188 | °C | |
Vicat Softening Temperature | ASTMD152512 | 176 | °C | |
-- | ISO306/B50 | 176 | °C | |
-- | ISO306/B120 | 175 | °C | |
Ball PressureTest | 75°C | IEC60695-10-2 | Pass | |
Coefficient of Linear Thermal Expansion | MD:-40到95°C | ASTME831 | 2.4E-05 | cm/cm/°C |
MD:23到80°C | ISO11359-2 | 2.3E-05 | cm/cm/°C | |
TD:-40to95°C | ASTME831 | 1.1E-04 | cm/cm/°C | |
TD:23to80°C | ISO11359-2 | 1.2E-04 | cm/cm/°C | |
Heat Deflection Temperature | 0.45MPa,未退火,6.40mm | ASTMD648 | 221 | °C |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
23°C | ISO179/1eA | 11 | kJ/m² | |
Notched Izod Impact Strength | -30°C | ASTMD256 | 74 | J/m |
23°C | ASTMD256 | 90 | J/m | |
-30°C | ISO180/1A | 8.5 | kJ/m² | |
23°C | ISO180/1A | 10 | kJ/m² | |
Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 13.4 | J |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Flame Rating | 0.8mm,TestingbySABIC | UL94 | V-0 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.