MMW-HDPE TOTAL Polyethylene HDPE HL 428
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792 | 0.947 g/cm³ | |
| melt mass-flow rate | ASTM D1238 | 0.28 g/10min | |
| ASTM D1238 | 20 g/10min |
| film | Test Condition | Test Method | Test Result |
|---|---|---|---|
| film thickness | 25 µm | ||
| Secant modulus | ASTM D882A | 710 MPa | |
| ASTM D882A | 1000 MPa | ||
| tensile strength | ASTM D882A | 24.1 MPa | |
| ASTM D882A | 23.4 MPa | ||
| ASTM D882A | 25.5 MPa | ||
| ASTM D882A | 26.2 MPa | ||
| ASTM D882A | 54.5 MPa | ||
| ASTM D882A | 62.1 MPa | ||
| Dart impact | ASTM D1709A | <50 g | |
| Elmendorf tear strength | ASTM D1922 | 28 g | |
| ASTM D1922 | 10 g | ||
| ASTM D1922 | 530 g | ||
| ASTM D1922 | 1500 g | ||
| Water Vapor Transmission Rate | ASTMF1249 | 7.8 g/m²/24hr | |
| ASTMF1249 | 11 g/m²/24hr | ||
| tensile strength | ASTM D882A | 39.3 MPa | |
| ASTM D882A | 18.6 MPa | ||
| elongation | ASTM D882A | 600 % | |
| ASTM D882A | 450 % | ||
| Tensile strain | ASTM D882A | 700 % | |
| ASTM D882A | 600 % | ||
| Dart impact | ASTM D1709A | 100 g |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melting temperature | ASTM D3417 | 131 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.