| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.12 g/cm³ |
| melt mass-flow rate | | ASTM D1238 | 15 g/10min |
| Shrinkage rate | | 内部方法 | 0.55 % |
| Water absorption rate | | ASTM D570 | 0.10 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| UL flame retardant rating | | UL 94 | HB |
| Hot filament ignition temperature | | IEC 60695-2-13 | 650 °C |
| Limiting Oxygen Index | | ASTM D2863 | 21 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| elongation | Break | ASTM D638 | 50 % |
| Flexural modulus | | ASTM D790 | 2250 MPa |
| tensile strength | Yield | ASTM D638 | 50.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 200 J/m |
| Impact strength of cantilever beam gap | | ASTM D256 | 300 J/m |
| Impact strength of cantilever beam gap | | ASTM D256 | 400 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 1 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 90.0 °C |
| vicat | | ASTM D15252 | 110 °C |
| ball-indentation hardness | | IEC 335 | 通过 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.