PC/ABS IP1000 BK SABIC INNOVATIVE SINGAPHORE

Form：Granules | Grade：Injection grade

Properties:

Flame retardantHigh impact resistance

Typical Applications:

Automotive interior partsElectrical applications

Supplier(0)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Automotive interior parts \| Electrical applications
Properties:	Flame retardant \| High impact resistance

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Instrumented impact	-30℃-30°C	ASTM D 3763	57	J
Instrumented impact	Instrumented impact	23℃23°C	ASTM D 3763	51	J
Impact strength of cantilever beam gap	-30℃-30°C	ASTM D256	500	J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23℃23°C	ASTM D256	680	J/m
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Bending modulus	1.30 mm/min，50 mmSpan1.3 mm/min，50mmSpan	ASTM D790	2270	Mpa
bending strength	Yield，1.30 mm/min，50 mm跨度Yield，1.3 mm/min，50mmSpan	ASTM D790	86	Mpa
Tensile modulus	50 mm/min50 mm / min	ASTM D638	2240	Mpa
Tensile strain Tensile strain 51mm/min	Break，50 mm/minBreak	ASTM D638	120	%
Tensile strain Tensile strain 50mm/min	Yield，50 mm/minYield	ASTM D638	5	%
tensile strength	Break，50 mm/minBreak，51mm/min	ASTM D638	55	Mpa
tensile strength	tensile strength	Yield，50 mm/minYield，50mm/min	ASTM D638	53	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear expansion coefficient, -40 ℃ to 41 ℃,	Across FlowTransverse	GB 1040	0.000080	1/℃
Linear expansion coefficient, -40 ℃ to 40 ℃,	FlowFlow	GB 1040	0.000080	1/℃
Hot deformation temperature	6.4mm6.4mm	ASTM D 648	110	°C
Hot deformation temperature	Hot deformation temperature	3.2mm3.2mm	ASTM D 648	129	°C
Vicat softening temperature		ASTM D1525	126	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	260℃，5.0kg260℃/5.0 kgf	ASTM D1238	13.5	g/10min
Shrinkage rate	TD：3.2 mmTransverse	Internal Method	0.5 - 0.7	%
Shrinkage rate	Shrinkage rate	MD：3.2 mmFlow	Internal Method	0.5 - 0.7	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.