PBT HR5330HF-NC010 DUPONT USA

Form：Granules | Grade：Injection grade

Properties:

Hydrolysis resistanceGlass fiber reinforcedFiller: Glass fiber reinf30% filler by weight

Typical Applications:

Electronic and electrical components

Supplier(1)

Product Description

Certificates(1)

Datasheet

Product Description

Typical Applications:	Electronic and electrical components
Properties:	Hydrolysis resistance \| Glass fiber reinforced \| Filler: Glass fiber reinf \| 30% filler by weight

Certificates

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap	23°C	ISO 180/1A	14	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-40°C	ISO 180/1A	11	kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	70	kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179/1eA	13	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C	ISO 179/1eA	12	kJ/m²
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	65	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
Burning rate	1.00mm	ISO 3795	30	mm/min
UL flame retardant rating	0.75mm	UL 94	HB
Flammability level	0.75mm	IEC 60695-11-10,-20	HB
Extreme Oxygen Index		ISO 4589-2	19	%
FMVSS flammability		FMVSS302	B
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Poisson's ratio		ISO 527	0.34
bending strength		ISO 178	200	Mpa
Bending modulus		ISO 178	7700	Mpa
Tensile strain	Break	ISO 527-2	3.5	%
tensile strength	Break	ISO 527-2	132	Mpa
Impact strength of cantilever beam gap	23 ℃, Type 1, Notch A	ISO 180	16.3	KJ/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-40 ℃, Type 1, Notch A	ISO 180	11.1	KJ/m
Charpy Notched Impact Strength	23 ℃, Type 1, Edgewise, Notch A	ISO 179	14.9	KJ/m
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30 ℃, Type 1, Edgewise, Notch A	ISO 179	11.5	KJ/m
Impact strength of simply supported beam without notch	23 ℃, Type 1, Edgewise	ISO 179	75.1	KJ/m
bending strength	23℃	ISO 178	203	MPa
Bending modulus	23℃	ISO 178	7800	MPa
Tensile modulus	23℃	ISO 527-1	8500	MPa
elongation	23℃，Yield	ISO 527-1	3.5	%
Tensile stress	23℃，Yield	ISO 527-1	134	MPa
Tensile modulus		ISO 527-2	8500	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.80 Mpa，Unannealed	ISO 75B-1	207	℃
Hot deformation temperature	Hot deformation temperature	0.45 Mpa，Unannealed	ISO 75B-1	221	℃
Melting temperature		ISO 3146	225	℃
Linear coefficient of thermal expansion	TD：-40to23°C	ISO 11359-2	9E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：55to160°C	ISO 11359-2	1.5E-04	cm/cm/°C
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	221	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	207	°C
Vicat softening temperature		ISO 306/B50	215	°C
Melting temperature		ISO 11357-3	225	°C
Linear coefficient of thermal expansion	MD：--	ISO 11359-2	2E-05	cm/cm/°C
	Linear coefficient of thermal expansion	MD：-40to23°C	ISO 11359-2	2.5E-05	cm/cm/°C
		Linear coefficient of thermal expansion	MD：55to160°C	ISO 11359-2	1.5E-05	cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：--	ISO 11359-2	1.5E-04	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ISO 1183	1.5
MediumDensity			1.29	g/cm³
density		ISO 1183	1.50	g/cm³
Shrinkage rate	TD	ISO 294-4	1.0	%
Shrinkage rate	Shrinkage rate	MD	ISO 294-4	0.30	%
Water absorption rate	Saturation,23°C,2.00mm	ISO 62	0.35	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,2.00mm,50%RH	ISO 62	0.15	%
Stickiness		ISO 307	95.0	cm³/g
FlowLength2	2.00mm，FlowLength		350	mm
Top out temperature			170	°C
SpecificHeatCapacity of Melt			1730	J/kg/°C
ThermalConductivityofMelt			0.28	W/m/K
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dissipation factor	100Hz	IEC 60250	2.5E-03
Dissipation factor	Dissipation factor	1MHz	IEC 60250	0.020
Compared to the anti leakage trace index		IEC 60112	PLC 1
Surface resistivity		IEC 60093	1E+13	ohms
Volume resistivity		IEC 60093	>1.0E+15	ohms·cm
Dielectric strength	--	IEC 60243-1	44	KV/mm
Dielectric strength	Dielectric strength	1.00mm5	IEC 60243-1	31	KV/mm
Relative permittivity	100Hz	IEC 60250	4.40
Relative permittivity	Relative permittivity	1MHz	IEC 60250	4.10
Dissipation factor	100Hz	ASTM D150	2.5E-03
	Dissipation factor	1kHz	ASTM D150	7E-03
	Dissipation factor	Dissipation factor	1MHz	ASTM D150	0.020

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.