Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 0.900 g/cm³ |
| melt mass-flow rate | | ISO 1133 | 25 g/10min |
| spiral flow length | | 内部方法 | 74.0 cm |
| Shrinkage rate | | 内部方法 | 1.0to1.4 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ISO 2039-2 | 70 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| gloss | | ASTM D523 | 90 |
| Haze ratio | | ISO 14782 | 10 % |
| Haze ratio | | ISO 14782 | 25 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2 | 750 MPa |
| tensile strength | Yield | ISO 527-2 | 22.0 MPa |
| Nominal tensile fracture strain | | ISO 527-2 | >400 % |
| Flexural modulus | | ISO 178 | 750 MPa |
| bending strength | | ISO 178 | 25.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179 | 2.0 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179 | 8.0 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/B | 70.0 °C |
| vicat | | ISO 306 | 110 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.