K(Q)胶 STYROLUX 684D

Properties:
High transparency
High Impact and GPPS Blen
Also suitable for injecti
Blow molding
Compare

Technical Data Sheet

Basic performance	Test Method	Test Result
Moisture absorption rate	ISO 62	0.07 %
Volume Flow Index	ISO 1133	11 CM
density	ISO 1183	1.01 g/cm
Water absorption rate	ISO 62	0.07 %

Mechanical properties	Test Method	Test Result
Impact strength of a simply supported beam without gaps	ISO 179/1eU	100/30 KJ/m
Shore hardness (A/D)	ISO 868	D58
Elongation	ISO 527-2	>50 %
Impact strength of notched simply supported beam	ISO 179/1eA	4/3 KJ/m
	ISO 527-2	2.3 %
Yang's modulus	ISO 527-2	1550 Mpa
Yield tensile strength	ISO 527-2	28 Mpa

Electrical performance	Test Method	Test Result
dielectric strength	IEC 93	140 KV/mm
dielectric constant	IEC 250	2.5
Surface Resistivity	IEC 243/1	>10
	IEC 93	>10 Ω.cm

Thermal performance	Test Method	Test Result
Heat distortion temperature	ISO 75	55 °C
UL94	UL 94	HB/HB CLASS
		180-250 °C
vicat	ISO 306	59 °C
Injection molding mold temperature		30-50 °C
Extrusion molding melting temperature		190-230 °C
vicat	ISO 306	85 °C
Heat distortion temperature	ISO 75	75 °C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.