PP Piolen® P T20A37 PiO Kunststoffe GmbH & Co KG

Properties:
Filler PiO Kunststoffe German PiO Kunststoffe
Usages:
Shell furniture
Compare

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-40°C	ISO 179/1eU	18 kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179/1eA	6.3 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-40°C	ISO 179/1eA	2.3 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.8mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
Tensile strain	Break	ISO 527-2	45 %
tensile strength	Break	ISO 527-2	25.0 MPa
tensile strength	tensile strength	Yield	ISO 527-2	28.0 MPa
Bending modulus		ISO 178	2350 MPa

thermal performance	Test Condition	Test Method	Test Result
Crystallization peak temperature	DSC	ISO 3146	160to170 °C
Vicat softening temperature	--	ISO 306/B	77.0 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/A	146 °C

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	230°C/2.16kg	ISO 1133	13 g/10min
density		ISO 1183	1.04 g/cm³

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.