Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | ISO62 | 1.3 % |
| Water absorption rate | | ISO62 | 2.9 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | V-2 |
| UL flame retardant rating | | UL94 | V-2 |
| Burning wire flammability index | | IEC60695-2-12 | 650 °C |
| GlowWireIgnitionTemperature | | IEC60695-2-13 | 650 °C |
| Limiting Oxygen Index | | ISO4589-2 | 26 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2/1A | 3200 Mpa |
| tensile strength | | ASTMD638 | 85.0 Mpa |
| Tensile stress | | ISO527-2/1A | 85.0 Mpa |
| Tensile stress | | ISO527-2/1A | 55.0 Mpa |
| Tensile strain | | ISO527-2 | 4.5 % |
| elongation | | ASTMD638 | 30 % |
| Tensile strain | | ISO527-2 | >30 % |
| Flexural modulus | | ASTMD790 | 3000 Mpa |
| Flexural modulus | | ISO178 | 2800 Mpa |
| bending strength | | ASTMD790 | 125 Mpa |
| Bending stress | | ISO178 | 120 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO179/1eU | NoBreak |
| | ISO180/1U | NoBreak |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC60093 | 1E+15 ohms |
| Volume resistivity | | IEC60093 | 1E+15 ohms·cm |
| dielectric strength | | IEC60243-1 | 25 KV/mm |
| | IEC60250 | 2.90 |
| Dissipation Factor | | IEC60250 | 0.030 |
| CTI | | IEC60112 | 600 V |
| CTI | | IEC60112 | 525 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ASTMD648 | 220 °C |
| | ISO75-2/Bf | 200 °C |
| | ISO75-2/Af | 75.0 °C |
| melting temperature | | ISO11357-3 | 263 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.