ASA Luran®S 797SE UV-WHP29435 INEOS STYRO KOREA
33
- Properties:High mobilityHigh impact resistance
- Usages:Fitness equipmentbuilding materialsCastersProfileAutomotive sectorApplication in the automosporting goods
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ISO1183 | 1.07 | g/cm³ | |
| Apparent density | 0.59 | g/cm³ | ||
| Melt Volume-Flow Rate (MVR) | 220°C/10.0kg | ISO1133 | 5.50 | cm3/10min |
| Shrinkage rate | ISO294-4 | 0.50to0.90 | % | |
| Water absorption rate | 饱和,23°C | ISO62 | 1.7 | % |
| 平衡,23°C,50%RH | ISO62 | 0.35 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ISO527-2 | 2000 | Mpa | |
| tensile strength | 屈服,23°C | ISO527-2 | 42.0 | Mpa |
| elongation | 屈服,23°C | ISO527-2 | 3.5 | % |
| Tensile creep modulus | 1000hr | ISO899-1 | 1100 | Mpa |
| bending strength | ISO178 | 60.0 | Mpa | |
| Charpy Notched Impact Strength | -30°C | ISO179 | 9.0 | kJ/m² |
| 23°C | ISO179 | 40 | kJ/m² | |
| Impact strength of cantilever beam gap | -30°C | ISO180/A | 10 | kJ/m² |
| 23°C | ISO180/A | 30 | kJ/m² | |
| Ball pressure hardness | ISO2039-1 | 65.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Annealed | ISO75-2/B | 100 | °C |
| 1.8MPa,Annealed | ISO75-2/A | 95.0 | °C | |
| vicat softening point | -- | ISO306/A50 | 104 | °C |
| -- | ISO306/B50 | 90.0 | °C | |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 8.0E-5to1.1E-4 | cm/cm/°C |
| thermal conductivity | DIN52612 | 0.17 | W/m/K |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC60093 | 1E+13 | ohms | |
| Volume resistivity | IEC60093 | 1E+14 | ohms·cm | |
| Dielectric constant | 100Hz | IEC60250 | 3.80 | |
| Dissipation factor | 100Hz | IEC60250 | 9E-03 | |
| 1MHz | IEC60250 | 0.026 |
| film | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Elongation MD | 断裂 | ISO527-3 | 11 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.