Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | | 1.25 g/cm³ |
| melt mass-flow rate | | | 10 g/10min |
| Melt volume flow rate | | | 9.50 cm³/10min |
| Shrinkage rate | | | 1.2到1.3 % |
| Water absorption rate | | | 0.40 % |
| Crystallinity | | | 60到70 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | | 67 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| Temperature of Use | | | -30到120 °C |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179/1eA | 2.7 kJ/m² |
| Charpy Notched Impact Strength | | ISO179/1eA | 1.4 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | 30 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | 无断裂 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | | 1140到1900 MPa |
| Tensile stress | Yield | | 24.0到27.0 MPa |
| Tensile strain | Break | | 6.0到9.0 % |
| Bending stress | | | 35.0 MPa |
| Bending stress | | | 29.0 MPa |
| Bending stress | | | 6.6 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/A | 59.0 °C |
| vicat | | ISO306/A120 | 147 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.